Manganese electrodeposition from urea-rich electrolyte
Апстракт
Pure manganese coatings were prepared on the steel (AISI 4340) electrode by a non-conventional electrodeposition method, in the presence of 8 mol dm(-3) of urea as a plating additive. The influence of urea on the electrodeposition of Mn was investigated by cyclic voltammetry. The morphology of the coatings was studied by scanning electron microscopy (SEM), and their elemental composition by energy dispersive X-ray spectrometry (EDS). The results showed that the presence of urea in the solution increased the current efficiency for metal reduction for around 20%, and depending on the applied deposition potential, urea may act either as a complexing agent or through the adsorption mechanism. Moreover, urea improves the characteristics of Mn deposits, i.e. their adhesiveness, porosity, compactness, and appearance. Except for oxygen, as part of the Mn corrosion product at the coating surface, no carbon or nitrogen incorporation was detected in the deposits by EDS.
Кључне речи:
urea / electrodeposition / Mn coating / morphologyИзвор:
Macedonian Journal of Chemistry and Chemical Engineering, 2015, 34, 2, 277-285Издавач:
- Soc Chemists Technologists Madeconia, Skopje
Финансирање / пројекти:
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45019)
- 36050
DOI: 10.20450/mjcce.2015.588
ISSN: 1857-5552
WoS: 000368505500007
Scopus: 2-s2.0-84956632801
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Vuruna, Mladen AU - Bucko, Mihael AU - Radović, Ljubica AU - Bajat, Jelena PY - 2015 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3088 AB - Pure manganese coatings were prepared on the steel (AISI 4340) electrode by a non-conventional electrodeposition method, in the presence of 8 mol dm(-3) of urea as a plating additive. The influence of urea on the electrodeposition of Mn was investigated by cyclic voltammetry. The morphology of the coatings was studied by scanning electron microscopy (SEM), and their elemental composition by energy dispersive X-ray spectrometry (EDS). The results showed that the presence of urea in the solution increased the current efficiency for metal reduction for around 20%, and depending on the applied deposition potential, urea may act either as a complexing agent or through the adsorption mechanism. Moreover, urea improves the characteristics of Mn deposits, i.e. their adhesiveness, porosity, compactness, and appearance. Except for oxygen, as part of the Mn corrosion product at the coating surface, no carbon or nitrogen incorporation was detected in the deposits by EDS. PB - Soc Chemists Technologists Madeconia, Skopje T2 - Macedonian Journal of Chemistry and Chemical Engineering T1 - Manganese electrodeposition from urea-rich electrolyte EP - 285 IS - 2 SP - 277 VL - 34 DO - 10.20450/mjcce.2015.588 ER -
@article{ author = "Vuruna, Mladen and Bucko, Mihael and Radović, Ljubica and Bajat, Jelena", year = "2015", abstract = "Pure manganese coatings were prepared on the steel (AISI 4340) electrode by a non-conventional electrodeposition method, in the presence of 8 mol dm(-3) of urea as a plating additive. The influence of urea on the electrodeposition of Mn was investigated by cyclic voltammetry. The morphology of the coatings was studied by scanning electron microscopy (SEM), and their elemental composition by energy dispersive X-ray spectrometry (EDS). The results showed that the presence of urea in the solution increased the current efficiency for metal reduction for around 20%, and depending on the applied deposition potential, urea may act either as a complexing agent or through the adsorption mechanism. Moreover, urea improves the characteristics of Mn deposits, i.e. their adhesiveness, porosity, compactness, and appearance. Except for oxygen, as part of the Mn corrosion product at the coating surface, no carbon or nitrogen incorporation was detected in the deposits by EDS.", publisher = "Soc Chemists Technologists Madeconia, Skopje", journal = "Macedonian Journal of Chemistry and Chemical Engineering", title = "Manganese electrodeposition from urea-rich electrolyte", pages = "285-277", number = "2", volume = "34", doi = "10.20450/mjcce.2015.588" }
Vuruna, M., Bucko, M., Radović, L.,& Bajat, J.. (2015). Manganese electrodeposition from urea-rich electrolyte. in Macedonian Journal of Chemistry and Chemical Engineering Soc Chemists Technologists Madeconia, Skopje., 34(2), 277-285. https://doi.org/10.20450/mjcce.2015.588
Vuruna M, Bucko M, Radović L, Bajat J. Manganese electrodeposition from urea-rich electrolyte. in Macedonian Journal of Chemistry and Chemical Engineering. 2015;34(2):277-285. doi:10.20450/mjcce.2015.588 .
Vuruna, Mladen, Bucko, Mihael, Radović, Ljubica, Bajat, Jelena, "Manganese electrodeposition from urea-rich electrolyte" in Macedonian Journal of Chemistry and Chemical Engineering, 34, no. 2 (2015):277-285, https://doi.org/10.20450/mjcce.2015.588 . .