Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium
2016
Authors
Nikolić, VesnaKamberović, Željko
Korać, Marija
Anđić, Zoran
Mihajlović, Aleksandar
Uljarević, Jelena B.
Article (Published version)
Metadata
Show full item recordAbstract
The aim of this study was comparative analysis of catalysts with 5 and 20 wt.% Ni loading, with and without Pd additive, and it included: determination of reduction degrees, investigation on microstructure by scanning electron microscopy and chemical analysis by energy-dispersive spectroscopy. Ni/Al2O3 and Ni-Pd/Al2O3 catalysts supported on alpha-Al2O3-based foams were synthesized by aerosol assisted impregnation. Impregnation of the foams by ultrasonically aerosolized chlorides was followed by drying at 473 K and hydrogen reduction at 533 and 633 K. Lower Ni loading resulted in higher reduction degrees. Ni loading of 20 wt.% enabled relatively uniform coverage of the foam with a metallic coating. Nearly complete reduction was achieved at both temperatures with activity modifier (Pd). Reduction degrees reached 99.4 and 98.2 wt.% at 533 K for 5 and 20 wt.% of Ni, respectively.
Keywords:
catalysts / Ni / Pd / modification / alpha-Al2O3-based foam / aerosol assisted impregnationSource:
Hemijska industrija, 2016, 70, 2, 137-142Publisher:
- Savez hemijskih inženjera, Beograd
Funding / projects:
- Innovative synergy of by-products, waste minimization and clean technologies in metallurgy (RS-34033)
DOI: 10.2298/HEMIND140928090N
ISSN: 0367-598X
WoS: 000376274600004
Scopus: 2-s2.0-84966573916
Collections
Institution/Community
Tehnološko-metalurški fakultetTY - JOUR AU - Nikolić, Vesna AU - Kamberović, Željko AU - Korać, Marija AU - Anđić, Zoran AU - Mihajlović, Aleksandar AU - Uljarević, Jelena B. PY - 2016 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3266 AB - The aim of this study was comparative analysis of catalysts with 5 and 20 wt.% Ni loading, with and without Pd additive, and it included: determination of reduction degrees, investigation on microstructure by scanning electron microscopy and chemical analysis by energy-dispersive spectroscopy. Ni/Al2O3 and Ni-Pd/Al2O3 catalysts supported on alpha-Al2O3-based foams were synthesized by aerosol assisted impregnation. Impregnation of the foams by ultrasonically aerosolized chlorides was followed by drying at 473 K and hydrogen reduction at 533 and 633 K. Lower Ni loading resulted in higher reduction degrees. Ni loading of 20 wt.% enabled relatively uniform coverage of the foam with a metallic coating. Nearly complete reduction was achieved at both temperatures with activity modifier (Pd). Reduction degrees reached 99.4 and 98.2 wt.% at 533 K for 5 and 20 wt.% of Ni, respectively. PB - Savez hemijskih inženjera, Beograd T2 - Hemijska industrija T1 - Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium EP - 142 IS - 2 SP - 137 VL - 70 DO - 10.2298/HEMIND140928090N ER -
@article{ author = "Nikolić, Vesna and Kamberović, Željko and Korać, Marija and Anđić, Zoran and Mihajlović, Aleksandar and Uljarević, Jelena B.", year = "2016", abstract = "The aim of this study was comparative analysis of catalysts with 5 and 20 wt.% Ni loading, with and without Pd additive, and it included: determination of reduction degrees, investigation on microstructure by scanning electron microscopy and chemical analysis by energy-dispersive spectroscopy. Ni/Al2O3 and Ni-Pd/Al2O3 catalysts supported on alpha-Al2O3-based foams were synthesized by aerosol assisted impregnation. Impregnation of the foams by ultrasonically aerosolized chlorides was followed by drying at 473 K and hydrogen reduction at 533 and 633 K. Lower Ni loading resulted in higher reduction degrees. Ni loading of 20 wt.% enabled relatively uniform coverage of the foam with a metallic coating. Nearly complete reduction was achieved at both temperatures with activity modifier (Pd). Reduction degrees reached 99.4 and 98.2 wt.% at 533 K for 5 and 20 wt.% of Ni, respectively.", publisher = "Savez hemijskih inženjera, Beograd", journal = "Hemijska industrija", title = "Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium", pages = "142-137", number = "2", volume = "70", doi = "10.2298/HEMIND140928090N" }
Nikolić, V., Kamberović, Ž., Korać, M., Anđić, Z., Mihajlović, A.,& Uljarević, J. B.. (2016). Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium. in Hemijska industrija Savez hemijskih inženjera, Beograd., 70(2), 137-142. https://doi.org/10.2298/HEMIND140928090N
Nikolić V, Kamberović Ž, Korać M, Anđić Z, Mihajlović A, Uljarević JB. Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium. in Hemijska industrija. 2016;70(2):137-142. doi:10.2298/HEMIND140928090N .
Nikolić, Vesna, Kamberović, Željko, Korać, Marija, Anđić, Zoran, Mihajlović, Aleksandar, Uljarević, Jelena B., "Nickel-based catalysts: Dependence of properties on nickel loading and modification with palladium" in Hemijska industrija, 70, no. 2 (2016):137-142, https://doi.org/10.2298/HEMIND140928090N . .