Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing
Apstrakt
The paper presents static and dynamic tests of carbon/epoxy composite materials with fiber orientation at 0 degrees/90 degrees and +/- 45 degrees. The main tensile properties were determined as a basis for subsequent dynamic tests, in which permanent dynamic strength, crack growth, and crack growth rate in the material due to the action of fatigue load were assessed. Comparisons were made regarding the structure of the tested specimens. Samples were obtained from prepregs with a specific density of 1600 kg/m(3). The tests were performed at room temperature. Scanning electron microscopy (SEM) was used to analyze the damage in the material during these tests, the mechanisms of their further damage progression and, the impact on the growth and growth rate of the initial crack in the material. The analysis of numerical results and micromechanical analysis confirmed the dominant role of the reinforcing structural element in the material in all performed tests. The obtained results are of gr...eat importance in the application of composite materials of such structures under different operating conditions and load regimes.
Ključne reči:
composite material / static tests / dynamic tests / crack growth / SEMIzvor:
Hemijska industrija, 2020, 74, 4, 257-264Izdavač:
- Savez hemijskih inženjera, Beograd
Finansiranje / projekti:
DOI: 10.2298/HEMIND200615022J
ISSN: 0367-598X
WoS: 000568682400004
Scopus: 2-s2.0-85093903582
Kolekcije
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Jelić, Aleksandra AU - Sekulić, Milica AU - Stamenović, Marina AU - Ugrinović, Vukašin AU - Putić, Slaviša PY - 2020 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/4399 AB - The paper presents static and dynamic tests of carbon/epoxy composite materials with fiber orientation at 0 degrees/90 degrees and +/- 45 degrees. The main tensile properties were determined as a basis for subsequent dynamic tests, in which permanent dynamic strength, crack growth, and crack growth rate in the material due to the action of fatigue load were assessed. Comparisons were made regarding the structure of the tested specimens. Samples were obtained from prepregs with a specific density of 1600 kg/m(3). The tests were performed at room temperature. Scanning electron microscopy (SEM) was used to analyze the damage in the material during these tests, the mechanisms of their further damage progression and, the impact on the growth and growth rate of the initial crack in the material. The analysis of numerical results and micromechanical analysis confirmed the dominant role of the reinforcing structural element in the material in all performed tests. The obtained results are of great importance in the application of composite materials of such structures under different operating conditions and load regimes. PB - Savez hemijskih inženjera, Beograd T2 - Hemijska industrija T1 - Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing EP - 264 IS - 4 SP - 257 VL - 74 DO - 10.2298/HEMIND200615022J ER -
@article{ author = "Jelić, Aleksandra and Sekulić, Milica and Stamenović, Marina and Ugrinović, Vukašin and Putić, Slaviša", year = "2020", abstract = "The paper presents static and dynamic tests of carbon/epoxy composite materials with fiber orientation at 0 degrees/90 degrees and +/- 45 degrees. The main tensile properties were determined as a basis for subsequent dynamic tests, in which permanent dynamic strength, crack growth, and crack growth rate in the material due to the action of fatigue load were assessed. Comparisons were made regarding the structure of the tested specimens. Samples were obtained from prepregs with a specific density of 1600 kg/m(3). The tests were performed at room temperature. Scanning electron microscopy (SEM) was used to analyze the damage in the material during these tests, the mechanisms of their further damage progression and, the impact on the growth and growth rate of the initial crack in the material. The analysis of numerical results and micromechanical analysis confirmed the dominant role of the reinforcing structural element in the material in all performed tests. The obtained results are of great importance in the application of composite materials of such structures under different operating conditions and load regimes.", publisher = "Savez hemijskih inženjera, Beograd", journal = "Hemijska industrija", title = "Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing", pages = "264-257", number = "4", volume = "74", doi = "10.2298/HEMIND200615022J" }
Jelić, A., Sekulić, M., Stamenović, M., Ugrinović, V.,& Putić, S.. (2020). Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing. in Hemijska industrija Savez hemijskih inženjera, Beograd., 74(4), 257-264. https://doi.org/10.2298/HEMIND200615022J
Jelić A, Sekulić M, Stamenović M, Ugrinović V, Putić S. Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing. in Hemijska industrija. 2020;74(4):257-264. doi:10.2298/HEMIND200615022J .
Jelić, Aleksandra, Sekulić, Milica, Stamenović, Marina, Ugrinović, Vukašin, Putić, Slaviša, "Micromechanical analysis of fatigue and crack growth in carbon-fiber epoxy composites based on mechanical testing" in Hemijska industrija, 74, no. 4 (2020):257-264, https://doi.org/10.2298/HEMIND200615022J . .