The influence of electroless plated chromium on printing properties of aluminum offset printing plate
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
A method for the improvement of the printing properties of offset printing forms is presented. Specimens of technical aluminum were electrochemically roughened and treated in different alkaline solutions of chromium chloride in order to chemically deposit a chromium layer. The composition of the surface layer was investigated by EDAX Chromium was found on the specimens that had been treated in an alkaline solution of chromium chloride. while no chromium was found on chemically untreated specimens or on specimens that had been treated in an alkaline solution without chromium chloride. The spectral reflectance from treated and non-treated specimens was also measured. The chromium-treated specimens were brighter than the non-chromium-treated ones. The wettability of the chromium-treated samples was compared with the wettability of the non-chromium treated samples by measuring the contact angle with water and the wetted area. The chromium-treated samples showed increased wettability compar...ed with the non-chromium-treated samples. A printing test was performed under real printing conditions. Control prints was analyzed densitometrically and statistically. The chromium-treated printing forms gave clearer prints than the non-chromium-treated printing forms under all printing conditions.
Кључне речи:
aluminum / chromium / electroless deposition / printing platesИзвор:
Journal of the Serbian Chemical Society, 2002, 67, 6, 445-455
DOI: 10.2298/JSC0206445Z
ISSN: 0352-5139
WoS: 000176608800008
Scopus: 2-s2.0-0036059371
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Živković, Predrag M. AU - Jovanovic, S AU - Ilic, N.M. AU - Popov, K.I. PY - 2002 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5379 AB - A method for the improvement of the printing properties of offset printing forms is presented. Specimens of technical aluminum were electrochemically roughened and treated in different alkaline solutions of chromium chloride in order to chemically deposit a chromium layer. The composition of the surface layer was investigated by EDAX Chromium was found on the specimens that had been treated in an alkaline solution of chromium chloride. while no chromium was found on chemically untreated specimens or on specimens that had been treated in an alkaline solution without chromium chloride. The spectral reflectance from treated and non-treated specimens was also measured. The chromium-treated specimens were brighter than the non-chromium-treated ones. The wettability of the chromium-treated samples was compared with the wettability of the non-chromium treated samples by measuring the contact angle with water and the wetted area. The chromium-treated samples showed increased wettability compared with the non-chromium-treated samples. A printing test was performed under real printing conditions. Control prints was analyzed densitometrically and statistically. The chromium-treated printing forms gave clearer prints than the non-chromium-treated printing forms under all printing conditions. T2 - Journal of the Serbian Chemical Society T1 - The influence of electroless plated chromium on printing properties of aluminum offset printing plate EP - 455 IS - 6 SP - 445 VL - 67 DO - 10.2298/JSC0206445Z ER -
@article{ author = "Živković, Predrag M. and Jovanovic, S and Ilic, N.M. and Popov, K.I.", year = "2002", abstract = "A method for the improvement of the printing properties of offset printing forms is presented. Specimens of technical aluminum were electrochemically roughened and treated in different alkaline solutions of chromium chloride in order to chemically deposit a chromium layer. The composition of the surface layer was investigated by EDAX Chromium was found on the specimens that had been treated in an alkaline solution of chromium chloride. while no chromium was found on chemically untreated specimens or on specimens that had been treated in an alkaline solution without chromium chloride. The spectral reflectance from treated and non-treated specimens was also measured. The chromium-treated specimens were brighter than the non-chromium-treated ones. The wettability of the chromium-treated samples was compared with the wettability of the non-chromium treated samples by measuring the contact angle with water and the wetted area. The chromium-treated samples showed increased wettability compared with the non-chromium-treated samples. A printing test was performed under real printing conditions. Control prints was analyzed densitometrically and statistically. The chromium-treated printing forms gave clearer prints than the non-chromium-treated printing forms under all printing conditions.", journal = "Journal of the Serbian Chemical Society", title = "The influence of electroless plated chromium on printing properties of aluminum offset printing plate", pages = "455-445", number = "6", volume = "67", doi = "10.2298/JSC0206445Z" }
Živković, P. M., Jovanovic, S., Ilic, N.M.,& Popov, K.I.. (2002). The influence of electroless plated chromium on printing properties of aluminum offset printing plate. in Journal of the Serbian Chemical Society, 67(6), 445-455. https://doi.org/10.2298/JSC0206445Z
Živković PM, Jovanovic S, Ilic N, Popov K. The influence of electroless plated chromium on printing properties of aluminum offset printing plate. in Journal of the Serbian Chemical Society. 2002;67(6):445-455. doi:10.2298/JSC0206445Z .
Živković, Predrag M., Jovanovic, S, Ilic, N.M., Popov, K.I., "The influence of electroless plated chromium on printing properties of aluminum offset printing plate" in Journal of the Serbian Chemical Society, 67, no. 6 (2002):445-455, https://doi.org/10.2298/JSC0206445Z . .