PZT ceramics obtained from mechanochemically synthesized powders
Samo za registrovane korisnike
2003
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.
Ključne reči:
Piezo ceramics / PZT / Piezoelectric properties / MechanochemistryIzvor:
Journal of Materials Science-Materials in Electronics, 2003, 14, 1, 37-41Izdavač:
- Kluwer Academic Publ, Dordrecht
DOI: 10.1023/A:1021527615661
ISSN: 0957-4522
WoS: 000179704600008
Scopus: 2-s2.0-0037287151
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Branković, Zorica AU - Branković, Goran AU - Varela, JA PY - 2003 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5398 AB - PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability. PB - Kluwer Academic Publ, Dordrecht T2 - Journal of Materials Science-Materials in Electronics T1 - PZT ceramics obtained from mechanochemically synthesized powders EP - 41 IS - 1 SP - 37 VL - 14 DO - 10.1023/A:1021527615661 ER -
@article{ author = "Branković, Zorica and Branković, Goran and Varela, JA", year = "2003", abstract = "PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.", publisher = "Kluwer Academic Publ, Dordrecht", journal = "Journal of Materials Science-Materials in Electronics", title = "PZT ceramics obtained from mechanochemically synthesized powders", pages = "41-37", number = "1", volume = "14", doi = "10.1023/A:1021527615661" }
Branković, Z., Branković, G.,& Varela, J.. (2003). PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics Kluwer Academic Publ, Dordrecht., 14(1), 37-41. https://doi.org/10.1023/A:1021527615661
Branković Z, Branković G, Varela J. PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics. 2003;14(1):37-41. doi:10.1023/A:1021527615661 .
Branković, Zorica, Branković, Goran, Varela, JA, "PZT ceramics obtained from mechanochemically synthesized powders" in Journal of Materials Science-Materials in Electronics, 14, no. 1 (2003):37-41, https://doi.org/10.1023/A:1021527615661 . .