Reflection and structural analyses of mirror-bright metal coatings
Само за регистроване кориснике
2004
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Reflection and structural analyses of different copper and zinc coatings were performed. The copper coatings were electrodeposited from a sulfate solution in the presence of thiourea, as well as in the presence of modified polyglycol ether, PEG 6000 and 3-mercaptopropanesulfonate.The zinc coating was electrodeposited from a sulfate solution in the presence of a dextrin/salicylaldehyde mixture. They were examined by STM and X-ray diffraction analysis, and measurements of the reflection of light from their surfaces were taken. The mean sizes of atomically flat parts of these surfaces were estimated by the STM software measurements,using options for the determination of the autocovariance function and the power spectral densityfunction. It was shown that the mean sizes of atomically flat parts of the copper coatings were several times greater than the mean size of atomically flat parts of the zinc coating. This difference probably leads to the difference in the maximum degrees of mirror r...eflection between copper and zinc coatings.
Кључне речи:
Copper / Electroplating / Scanning tunneling microscopy / X-ray diffraction / ZincИзвор:
Journal of Solid State Electrochemistry, 2004, 8, 526-531Издавач:
- Springer
Финансирање / пројекти:
- Ministarstvo prosvete, nauke i tehnološkog razvoja Republike Srbije (1806/2002)
- Ministarstvo prosvete, nauke i tehnološkog razvoja Republike Srbije (2018/2002)
DOI: 10.1007/s10008-003-0467-8
ISSN: 1432-8488
WoS: 000222354300002
Scopus: 2-s2.0-3242659743
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Nikolić, Nebojša D. AU - Rakočević, Zlatko Lj. AU - Popov, Konstantin I. PY - 2004 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5410 AB - Reflection and structural analyses of different copper and zinc coatings were performed. The copper coatings were electrodeposited from a sulfate solution in the presence of thiourea, as well as in the presence of modified polyglycol ether, PEG 6000 and 3-mercaptopropanesulfonate.The zinc coating was electrodeposited from a sulfate solution in the presence of a dextrin/salicylaldehyde mixture. They were examined by STM and X-ray diffraction analysis, and measurements of the reflection of light from their surfaces were taken. The mean sizes of atomically flat parts of these surfaces were estimated by the STM software measurements,using options for the determination of the autocovariance function and the power spectral densityfunction. It was shown that the mean sizes of atomically flat parts of the copper coatings were several times greater than the mean size of atomically flat parts of the zinc coating. This difference probably leads to the difference in the maximum degrees of mirror reflection between copper and zinc coatings. PB - Springer T2 - Journal of Solid State Electrochemistry T1 - Reflection and structural analyses of mirror-bright metal coatings EP - 531 SP - 526 VL - 8 DO - 10.1007/s10008-003-0467-8 ER -
@article{ author = "Nikolić, Nebojša D. and Rakočević, Zlatko Lj. and Popov, Konstantin I.", year = "2004", abstract = "Reflection and structural analyses of different copper and zinc coatings were performed. The copper coatings were electrodeposited from a sulfate solution in the presence of thiourea, as well as in the presence of modified polyglycol ether, PEG 6000 and 3-mercaptopropanesulfonate.The zinc coating was electrodeposited from a sulfate solution in the presence of a dextrin/salicylaldehyde mixture. They were examined by STM and X-ray diffraction analysis, and measurements of the reflection of light from their surfaces were taken. The mean sizes of atomically flat parts of these surfaces were estimated by the STM software measurements,using options for the determination of the autocovariance function and the power spectral densityfunction. It was shown that the mean sizes of atomically flat parts of the copper coatings were several times greater than the mean size of atomically flat parts of the zinc coating. This difference probably leads to the difference in the maximum degrees of mirror reflection between copper and zinc coatings.", publisher = "Springer", journal = "Journal of Solid State Electrochemistry", title = "Reflection and structural analyses of mirror-bright metal coatings", pages = "531-526", volume = "8", doi = "10.1007/s10008-003-0467-8" }
Nikolić, N. D., Rakočević, Z. Lj.,& Popov, K. I.. (2004). Reflection and structural analyses of mirror-bright metal coatings. in Journal of Solid State Electrochemistry Springer., 8, 526-531. https://doi.org/10.1007/s10008-003-0467-8
Nikolić ND, Rakočević ZL, Popov KI. Reflection and structural analyses of mirror-bright metal coatings. in Journal of Solid State Electrochemistry. 2004;8:526-531. doi:10.1007/s10008-003-0467-8 .
Nikolić, Nebojša D., Rakočević, Zlatko Lj., Popov, Konstantin I., "Reflection and structural analyses of mirror-bright metal coatings" in Journal of Solid State Electrochemistry, 8 (2004):526-531, https://doi.org/10.1007/s10008-003-0467-8 . .