Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution
Samo za registrovane korisnike
2005
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The corrosion behavior of mild steel and mild steel covered by electrochemically deposited (a) polyaniline (PANI) film, (b) epoxy coating
and (c) PANI/epoxy coating system in 0.1 M sulfuric acid solution were investigated by electrochemical impedance spectroscopy (EIS).
Electrochemical deposition of PANI film was performed from aqueous solution of 0.5 M sodium benzoate and 0.1 M aniline at constant
current density of 1.5 mA cm−2. Epoxy coatings on mild steel and mild steel modified by PANI film were deposited at constant voltage. It
was shown that thin PANI film had provided good corrosion protection of mild steel in 0.1 M sulfuric acid solution, and could be used for
modification of mild steel prior to epoxy coating deposition. The increased corrosion protection of mild steel by PANI/epoxy coating system
in the same solution was obtained.
Ključne reči:
polyaniline / epoxy / electropolymerization / benzoate / mild steel / corrosionIzvor:
Progress in Organic Coatings, 2005, 52, 4, 359-365Izdavač:
- Elsevier Science Sa, Lausanne
DOI: 10.1016/j.porgcoat.2004.05.009
ISSN: 0300-9440
WoS: 000228110100014
Scopus: 2-s2.0-17844399554
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Popović, MM AU - Grgur, Branimir AU - Mišković-Stanković, Vesna PY - 2005 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/815 AB - The corrosion behavior of mild steel and mild steel covered by electrochemically deposited (a) polyaniline (PANI) film, (b) epoxy coating and (c) PANI/epoxy coating system in 0.1 M sulfuric acid solution were investigated by electrochemical impedance spectroscopy (EIS). Electrochemical deposition of PANI film was performed from aqueous solution of 0.5 M sodium benzoate and 0.1 M aniline at constant current density of 1.5 mA cm−2. Epoxy coatings on mild steel and mild steel modified by PANI film were deposited at constant voltage. It was shown that thin PANI film had provided good corrosion protection of mild steel in 0.1 M sulfuric acid solution, and could be used for modification of mild steel prior to epoxy coating deposition. The increased corrosion protection of mild steel by PANI/epoxy coating system in the same solution was obtained. PB - Elsevier Science Sa, Lausanne T2 - Progress in Organic Coatings T1 - Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution EP - 365 IS - 4 SP - 359 VL - 52 DO - 10.1016/j.porgcoat.2004.05.009 ER -
@article{ author = "Popović, MM and Grgur, Branimir and Mišković-Stanković, Vesna", year = "2005", abstract = "The corrosion behavior of mild steel and mild steel covered by electrochemically deposited (a) polyaniline (PANI) film, (b) epoxy coating and (c) PANI/epoxy coating system in 0.1 M sulfuric acid solution were investigated by electrochemical impedance spectroscopy (EIS). Electrochemical deposition of PANI film was performed from aqueous solution of 0.5 M sodium benzoate and 0.1 M aniline at constant current density of 1.5 mA cm−2. Epoxy coatings on mild steel and mild steel modified by PANI film were deposited at constant voltage. It was shown that thin PANI film had provided good corrosion protection of mild steel in 0.1 M sulfuric acid solution, and could be used for modification of mild steel prior to epoxy coating deposition. The increased corrosion protection of mild steel by PANI/epoxy coating system in the same solution was obtained.", publisher = "Elsevier Science Sa, Lausanne", journal = "Progress in Organic Coatings", title = "Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution", pages = "365-359", number = "4", volume = "52", doi = "10.1016/j.porgcoat.2004.05.009" }
Popović, M., Grgur, B.,& Mišković-Stanković, V.. (2005). Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution. in Progress in Organic Coatings Elsevier Science Sa, Lausanne., 52(4), 359-365. https://doi.org/10.1016/j.porgcoat.2004.05.009
Popović M, Grgur B, Mišković-Stanković V. Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution. in Progress in Organic Coatings. 2005;52(4):359-365. doi:10.1016/j.porgcoat.2004.05.009 .
Popović, MM, Grgur, Branimir, Mišković-Stanković, Vesna, "Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution" in Progress in Organic Coatings, 52, no. 4 (2005):359-365, https://doi.org/10.1016/j.porgcoat.2004.05.009 . .