The thermal degradation of poly(diethyl fumarate)
Samo za registrovane korisnike
2006
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The kinetics and mechanism of the thermal degradation of poly(diethyl fumarate) (PDEF) were studied by thermogravimetry, as well as by analysis of the thermolysis volatiles and polymer residue. The characteristic mass loss temperatures were determined, as were the overall thermal degradation activation energies of three PDEF samples of varying molar mass. Ethylene and ethanol were present in the thermolysis volatiles at degradation temperatures below 300 degrees C, while diethyl fumarate was also evidenced at higher degradation temperatures. The amount of monomer increased with increasing degradation temperature. The dependence of the molar mass of the residual polymer on the degradation time and temperature was established and the number of main-chain scissions per monomer unit, s/P-0, calculated. A thermal degradation mechanism including de-esterification and random main-chain scission is proposed. The thermal degradation of PDEF was compared to the thermolysis of poly(ethyl methacry...late) (PEMA), poly(diethyl itaconate) (PDEI) and poly(ethyl acrylate) (PEA).
Ključne reči:
poly(diethyl fumarate) / thermal degradation / kinetics / mechanismIzvor:
Polymer Degradation and Stability, 2006, 91, 12, 3221-3229Izdavač:
- Elsevier Sci Ltd, Oxford
Finansiranje / projekti:
DOI: 10.1016/j.polymdegradstab.2006.07.007
ISSN: 0141-3910
WoS: 000243088200047
Scopus: 2-s2.0-33845438401
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Milovanović, Miloš AU - Bošković, Radomir AU - Tosić, Tomica AU - Katsikas, Lynne AU - Popović, Ivanka PY - 2006 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/993 AB - The kinetics and mechanism of the thermal degradation of poly(diethyl fumarate) (PDEF) were studied by thermogravimetry, as well as by analysis of the thermolysis volatiles and polymer residue. The characteristic mass loss temperatures were determined, as were the overall thermal degradation activation energies of three PDEF samples of varying molar mass. Ethylene and ethanol were present in the thermolysis volatiles at degradation temperatures below 300 degrees C, while diethyl fumarate was also evidenced at higher degradation temperatures. The amount of monomer increased with increasing degradation temperature. The dependence of the molar mass of the residual polymer on the degradation time and temperature was established and the number of main-chain scissions per monomer unit, s/P-0, calculated. A thermal degradation mechanism including de-esterification and random main-chain scission is proposed. The thermal degradation of PDEF was compared to the thermolysis of poly(ethyl methacrylate) (PEMA), poly(diethyl itaconate) (PDEI) and poly(ethyl acrylate) (PEA). PB - Elsevier Sci Ltd, Oxford T2 - Polymer Degradation and Stability T1 - The thermal degradation of poly(diethyl fumarate) EP - 3229 IS - 12 SP - 3221 VL - 91 DO - 10.1016/j.polymdegradstab.2006.07.007 ER -
@article{ author = "Milovanović, Miloš and Bošković, Radomir and Tosić, Tomica and Katsikas, Lynne and Popović, Ivanka", year = "2006", abstract = "The kinetics and mechanism of the thermal degradation of poly(diethyl fumarate) (PDEF) were studied by thermogravimetry, as well as by analysis of the thermolysis volatiles and polymer residue. The characteristic mass loss temperatures were determined, as were the overall thermal degradation activation energies of three PDEF samples of varying molar mass. Ethylene and ethanol were present in the thermolysis volatiles at degradation temperatures below 300 degrees C, while diethyl fumarate was also evidenced at higher degradation temperatures. The amount of monomer increased with increasing degradation temperature. The dependence of the molar mass of the residual polymer on the degradation time and temperature was established and the number of main-chain scissions per monomer unit, s/P-0, calculated. A thermal degradation mechanism including de-esterification and random main-chain scission is proposed. The thermal degradation of PDEF was compared to the thermolysis of poly(ethyl methacrylate) (PEMA), poly(diethyl itaconate) (PDEI) and poly(ethyl acrylate) (PEA).", publisher = "Elsevier Sci Ltd, Oxford", journal = "Polymer Degradation and Stability", title = "The thermal degradation of poly(diethyl fumarate)", pages = "3229-3221", number = "12", volume = "91", doi = "10.1016/j.polymdegradstab.2006.07.007" }
Milovanović, M., Bošković, R., Tosić, T., Katsikas, L.,& Popović, I.. (2006). The thermal degradation of poly(diethyl fumarate). in Polymer Degradation and Stability Elsevier Sci Ltd, Oxford., 91(12), 3221-3229. https://doi.org/10.1016/j.polymdegradstab.2006.07.007
Milovanović M, Bošković R, Tosić T, Katsikas L, Popović I. The thermal degradation of poly(diethyl fumarate). in Polymer Degradation and Stability. 2006;91(12):3221-3229. doi:10.1016/j.polymdegradstab.2006.07.007 .
Milovanović, Miloš, Bošković, Radomir, Tosić, Tomica, Katsikas, Lynne, Popović, Ivanka, "The thermal degradation of poly(diethyl fumarate)" in Polymer Degradation and Stability, 91, no. 12 (2006):3221-3229, https://doi.org/10.1016/j.polymdegradstab.2006.07.007 . .