Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
Microstructure evolution of the hot-rolled modified AA 5083 alloys during the two stage thermal treatment
(Savez inženjera metalurgije Srbije, Beograd, 2011)
The effects of the two stage heat treatment on the structure of two hot-rolled 5083 aluminum alloys without and with 0.12% Zr addition were investigated. Combination of the metallographic and transmission electron microscopy ...
Development of contemporary procedures for lead obtaining / Razvoj savremenih postupaka dobijanja olova
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Contemporary procedures of lead concentrates treatment were in different expansion during last thirty years. All procedures have in common the following: smelting reaction proceeds in solid-gas suspension, melting products ...
Dynamic recrystallization in M2 tool steel during friction welding
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Friction welding of M2 tool steel and 1730 quenched and tempered steel was performed with the aim to reveal the origin of extremely fine martensitic grain in M2 steel after welding. Taking into account thermomechanical ...
A two-stage metal valorisation process from electric arc furnace dust (eafd)
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper demonstrates possibility of separate zinc and lead recovery from coal composite pellets, composed of EAFD with other synergetic iron-bearing wastes and by-products (mill scale, pyrite-cinder, magnetite concentrate), ...
Influence of milling parameters on the preparation of fine tungsten and copper powders by mechanically induced self-propagating reaction / Uticaj parametara mlevenja na dobijanje finih prahova volframa i bakra mehanički iniciranom samorasprostirućom reakcijom
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Mechanically induced self-propagating reaction in planetary ball mill was realized in three different systems, CaWO4 (scheelite) + Mg, CuO + Ti and CuO + Zr. An influence of a ball diameter (from 5 to 41.2 mm) at three ...