Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
HCOOH oxidation on thin Pd layers on Au: Self-poisoning by the subsequent reaction of the reaction product
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The oxidation of HCOOH has been investigated on thin Pd layers ranging from 1 to 17 ML equivalents electrodeposited on polycrystalline Au substrate (Pd"Au). The results are compared to those on Pd black. Potentiodynamic ...
Hydrogen peroxide oxidation on passive iron in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1992)
The kinetics of hydrogen peroxide oxidation were studied on passive iron in alkaline solutions of pH ranging from 9.8 to 13.8, using the rotating disk electrode. Measurements were taken using the linear sweep technique. ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
Oxygen reduction on iron-Part VI. Processes in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1994)
The kinetics of oxygen reduction were studied on passivated iron in borate buffered and unbuffered solutions of pH ranging from 7.4 to 13.8. A rotating disk electrode was employed. The O2 reduction on iron under these ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Oxygen reduction on iron-IV. The reduction of hydrogen peroxide as the intermediate in oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1991)
The kinetics of hydrogen peroxide reduction were studied on iron in borate buffered and unbuffered solutions of pH ranging from 8.6 to 13.8, with and without the presence of chloride ions. A rotating disk electrode was ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Kinetic analysis of hydrogen evolution at Ni-Mo alloy electrodes
(Elsevier Science Ltd, 2000)
The hydrogen evolution reaction (HER) on Ni, Mo and MoNi intermetallic compound was investigated with ac impedance and dc polarization measurements in 1.0 mol dm-3 NaOH solution at 25 °C. The rate constants of the forward ...