Investigation of mechanism and kinetics of chalcopyrite concentrate oxidation process
(Croatian Metallurgical Society, 2008)
The oxidation process of chalcopyrite concentrate "Rudnik" (Serbia) was investigated by DTA-TG measurements under air conditions in the temperature range of 298 - 1173 K, as well as by XRD analysis of the oxidation products ...
Synthesis and sintering of Cu-Al2O3 nanocomposite powders produced by a thermochemical route
(Savez inženjera metalurgije Srbije, Beograd, 2007)
By hydrometallurgy and powder metallurgy along with prognosis of physical-chemical properties, a synthesis of new improved materials can be successfully performed with in advance pre-set properties which is conditioned by ...
Tensile properties of fiber-resin composites that consist of polyarmid fiber (Kevlar 129) and poly(vinilbutyral) / Zatezna svojstva polimernog kompozitnog materijala poliaramidna vlakna (Kevlar 129) - poli(vinilbutiral)(PVB)
(Savez inženjera metalurgije Srbije, Beograd, 2006)
Thanks to fact that composite material have usefully characteristic two or more materials, they are becoming more and more substitute standard materials in every field of technique they start to. In this study static ...
Characterization of nano-powder morphology obtained by ultrasonic spray pyrolysis
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Spherical nanosized particles of copper were synthesized by ultrasonic dispersion of solutions from copper sulphate in the temperature range of 800-900°C in hydrogen atmosphere. A controlled particle size was realized ...
Determination of AL2O3particle size in Cu-AL2O3 nanocomposite materials using UV spectrophotometry / Određivanje veličine čestica AL2O3 u nanokompozitnim materijalima iz sistema Cu-AL2O3 primenom UV spektrofotometrije
(Savez inženjera metalurgije Srbije, Beograd, 2008)
In order to achieve improved mechanical properties of dispersion strengthened nanocomposite, without influencing electrical and thermal conductivity it is necessary for dispersoide to be nano sized and uniformly distributed ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...