The nucleation behavior of k2o center dot tio2 center dot 3geo(2) undercooled melt
(University of Chemistry and Technology, Prague, 2009)
The nucleation of K2TiGe3O9 crystals in an undercooled melt of stoichiometric composition was studied. Volume nucleation with spherical morphology of the growing crystals was determined. The nucleation range is in the ...
The crystallization of potassium germanate glass with high content of niobium oxide
(University of Chemistry and Technology, Prague, 2012)
Potassium germanate glass with molar ratio [GeO2]/[K2O] = 1.2 and Nb2O5 content of 34 mol% have been synthesized by a melt-quenching method. The crystallization behavior under non-isothermal and isothermal crystallization ...
Thermal shock damage characterization of high temperature ceramics by non destructive test methods
(University of Chemistry and Technology, Prague, 2008)
In the present work a mixture of commercially available spinel, quartz (SiO2) and alumina (Al2O3) corresponding to cordierite stoichiometry was used as starting material for obtaining cordierite/SiC composite ceramics with ...
The crystallisation of calcium phosphate glass containing vanadium oxide
(University of Chemistry and Technology, Prague, 2007)
The crystallisation behaviour of calcium phosphate glass containing vanadium oxide was studied. Glass with a molar ratio of [CaO]/[P2O5] = 1.13 and a V2O5 content of 8 mol.% was prepared for the experiments. The crystallisation ...
Structural and crystallization characteristics of K 2 O· TiO 2 ·3GeO 2 glass / Strukturní a krystalizaèní charakteristiky k2o·tio2·3geo2 skel
(Institute of Chemical Technology, 2005)
Structure and crystallization of K 2 O·TiO 2 ·3GeO 2 glass have been investigated by means of Fourier transform infrared spectroscopy (FTIR), differential thermal analysis (DTA), differential scanning calorimetry (DSC), ...