Sintering behaviour of nanosized HAP powder
No Thumbnail
Authors
Veljović, Đorđe
Jokić, Bojan
Janković-Častvan, Ivona

Smičiklas, Ivana D.

Petrović, Rada

Janaćković, Đorđe

Article (Published version)

Metadata
Show full item recordAbstract
The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.
Keywords:
hydroxyapatite / sintering / nanostructureSource:
Key Engineering Materials, 2007, 330-332 I, 259-262Publisher:
- Trans Tech Publications Ltd, Durnten-Zurich
Funding / projects:
- Sinteza, struktura, svojstva i primena funkcionalnih nanostrukturnih keramičkih i biokeramičkih materijala (RS-142070)
- EUREKA E [3033]
Institution/Community
Tehnološko-metalurški fakultetTY - JOUR AU - Veljović, Đorđe AU - Jokić, Bojan AU - Janković-Častvan, Ivona AU - Smičiklas, Ivana D. AU - Petrović, Rada AU - Janaćković, Đorđe PY - 2007 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1021 AB - The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained. PB - Trans Tech Publications Ltd, Durnten-Zurich T2 - Key Engineering Materials T1 - Sintering behaviour of nanosized HAP powder EP - 262 SP - 259 VL - 330-332 I UR - https://hdl.handle.net/21.15107/rcub_technorep_1021 ER -
@article{ author = "Veljović, Đorđe and Jokić, Bojan and Janković-Častvan, Ivona and Smičiklas, Ivana D. and Petrović, Rada and Janaćković, Đorđe", year = "2007", abstract = "The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.", publisher = "Trans Tech Publications Ltd, Durnten-Zurich", journal = "Key Engineering Materials", title = "Sintering behaviour of nanosized HAP powder", pages = "262-259", volume = "330-332 I", url = "https://hdl.handle.net/21.15107/rcub_technorep_1021" }
Veljović, Đ., Jokić, B., Janković-Častvan, I., Smičiklas, I. D., Petrović, R.,& Janaćković, Đ.. (2007). Sintering behaviour of nanosized HAP powder. in Key Engineering Materials Trans Tech Publications Ltd, Durnten-Zurich., 330-332 I, 259-262. https://hdl.handle.net/21.15107/rcub_technorep_1021
Veljović Đ, Jokić B, Janković-Častvan I, Smičiklas ID, Petrović R, Janaćković Đ. Sintering behaviour of nanosized HAP powder. in Key Engineering Materials. 2007;330-332 I:259-262. https://hdl.handle.net/21.15107/rcub_technorep_1021 .
Veljović, Đorđe, Jokić, Bojan, Janković-Častvan, Ivona, Smičiklas, Ivana D., Petrović, Rada, Janaćković, Đorđe, "Sintering behaviour of nanosized HAP powder" in Key Engineering Materials, 330-332 I (2007):259-262, https://hdl.handle.net/21.15107/rcub_technorep_1021 .