The influence of hot-dip galvanized steel (HDG) surface pretreatment with phosphate coatings on the corrosion stability and adhesion characteristics of epoxy coatings electrodeposited on HDG steel was investigated. Phosphate coatings were deposited on hot-dip galvanized steel from baths with different concentrations of NaF (0.1, 0.5 and 1.0 g dm(-3)) and at different temperatures (50, 65 and 80 degrees C). The influence of fluoride ion concentration in the phosphating bath, as well as the deposition temperature of the bath, on the adhesion characteristics and corrosion stability of epoxy coatings on phosphated HDG steel was investigated. The dry and wet adhesions were measured by a direct pull-off standardized procedure, as well as indirectly by NMP test, while corrosion stability was investigated by electrochemical impedance spectroscopy (EIS). It was shown that under dry testing conditions all the samples exhibited very good adhesion. However, the different trends of adhesion loss of... different protective systems during exposure to corrosive agent (3% NaCl solution) were observed. The lowest adhesion values were obtained for epoxy coating on hot-dip galvanized steel, while the phosphate pretreatments significantly increase the adhesion of epoxy coatings. The highest values of adhesion strength were obtained for epoxy coating on HDG steel modified by phosphate coating deposited at 65 degrees C with 0.5 g dm(-3) NaF in the phosphating bath. EIS measurements in 3% NaCl solution are in accordance with adhesion measurements, i.e. greater values of charge-transfer resistance and smaller values of double-layer capacitance were obtained, as compared to other protective systems.
TY - JOUR
AU - Bajat, Jelena
AU - Mišković-Stanković, Vesna
AU - Popić, Jovan P.
AU - Dražić, Dragutin M.
PY - 2008
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1241
AB - The influence of hot-dip galvanized steel (HDG) surface pretreatment with phosphate coatings on the corrosion stability and adhesion characteristics of epoxy coatings electrodeposited on HDG steel was investigated. Phosphate coatings were deposited on hot-dip galvanized steel from baths with different concentrations of NaF (0.1, 0.5 and 1.0 g dm(-3)) and at different temperatures (50, 65 and 80 degrees C). The influence of fluoride ion concentration in the phosphating bath, as well as the deposition temperature of the bath, on the adhesion characteristics and corrosion stability of epoxy coatings on phosphated HDG steel was investigated. The dry and wet adhesions were measured by a direct pull-off standardized procedure, as well as indirectly by NMP test, while corrosion stability was investigated by electrochemical impedance spectroscopy (EIS). It was shown that under dry testing conditions all the samples exhibited very good adhesion. However, the different trends of adhesion loss of different protective systems during exposure to corrosive agent (3% NaCl solution) were observed. The lowest adhesion values were obtained for epoxy coating on hot-dip galvanized steel, while the phosphate pretreatments significantly increase the adhesion of epoxy coatings. The highest values of adhesion strength were obtained for epoxy coating on HDG steel modified by phosphate coating deposited at 65 degrees C with 0.5 g dm(-3) NaF in the phosphating bath. EIS measurements in 3% NaCl solution are in accordance with adhesion measurements, i.e. greater values of charge-transfer resistance and smaller values of double-layer capacitance were obtained, as compared to other protective systems.
PB - Elsevier Science Sa, Lausanne
T2 - Progress in Organic Coatings
T1 - Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel
EP - 208
IS - 2
SP - 201
VL - 63
DO - 10.1016/j.porgcoat.2008.06.002
UR - conv_3064
ER -
@article{
author = "Bajat, Jelena and Mišković-Stanković, Vesna and Popić, Jovan P. and Dražić, Dragutin M.",
year = "2008",
abstract = "The influence of hot-dip galvanized steel (HDG) surface pretreatment with phosphate coatings on the corrosion stability and adhesion characteristics of epoxy coatings electrodeposited on HDG steel was investigated. Phosphate coatings were deposited on hot-dip galvanized steel from baths with different concentrations of NaF (0.1, 0.5 and 1.0 g dm(-3)) and at different temperatures (50, 65 and 80 degrees C). The influence of fluoride ion concentration in the phosphating bath, as well as the deposition temperature of the bath, on the adhesion characteristics and corrosion stability of epoxy coatings on phosphated HDG steel was investigated. The dry and wet adhesions were measured by a direct pull-off standardized procedure, as well as indirectly by NMP test, while corrosion stability was investigated by electrochemical impedance spectroscopy (EIS). It was shown that under dry testing conditions all the samples exhibited very good adhesion. However, the different trends of adhesion loss of different protective systems during exposure to corrosive agent (3% NaCl solution) were observed. The lowest adhesion values were obtained for epoxy coating on hot-dip galvanized steel, while the phosphate pretreatments significantly increase the adhesion of epoxy coatings. The highest values of adhesion strength were obtained for epoxy coating on HDG steel modified by phosphate coating deposited at 65 degrees C with 0.5 g dm(-3) NaF in the phosphating bath. EIS measurements in 3% NaCl solution are in accordance with adhesion measurements, i.e. greater values of charge-transfer resistance and smaller values of double-layer capacitance were obtained, as compared to other protective systems.",
publisher = "Elsevier Science Sa, Lausanne",
journal = "Progress in Organic Coatings",
title = "Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel",
pages = "208-201",
number = "2",
volume = "63",
doi = "10.1016/j.porgcoat.2008.06.002",
url = "conv_3064"
}
Bajat, J., Mišković-Stanković, V., Popić, J. P.,& Dražić, D. M.. (2008). Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel. in Progress in Organic Coatings
Elsevier Science Sa, Lausanne., 63(2), 201-208.
https://doi.org/10.1016/j.porgcoat.2008.06.002
conv_3064
Bajat J, Mišković-Stanković V, Popić JP, Dražić DM. Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel. in Progress in Organic Coatings. 2008;63(2):201-208.
doi:10.1016/j.porgcoat.2008.06.002
conv_3064 .
Bajat, Jelena, Mišković-Stanković, Vesna, Popić, Jovan P., Dražić, Dragutin M., "Adhesion characteristics and corrosion stability of epoxy coatings electrodeposited on phosphated hot-dip galvanized steel" in Progress in Organic Coatings, 63, no. 2 (2008):201-208,
https://doi.org/10.1016/j.porgcoat.2008.06.002 .,
conv_3064 .