Effect of heating rate on precipitation of peak-aged Al-Li (8091) alloy: A quantitative approach

dc.creatorNovitović, Olivera
dc.creatorKamberović, Željko
dc.creatorNovitović, Aleksandar
dc.date.accessioned2021-03-10T11:15:39Z
dc.date.available2021-03-10T11:15:39Z
dc.date.issued2010
dc.identifier.issn0354-6306
dc.identifier.urihttp://TechnoRep.tmf.bg.ac.rs/handle/123456789/1588
dc.description.abstractSamples of Al-Li (8091) alloy were solution treated at 540ºC for 30 min, water-quenched and continuously heated in oil at 0.05 and 0.1ºC/min rates, from room temperature to 190ºC when the peak hardness was achieved. Having reached 190ºC at a pre-determined heating rate samples were water-quenched followed by cooling in liquid nitrogen. Precipitate identification performed by transmission electron microscopy (TEM) revealed the presence of strengthening phases formed during heating to 190ºC: δ' (Al3Li), S (Al2CuMg), and β' (Al3Zr). Applying the method of quantitative metallographic analysis (light microscopy and TEM) size, shape, density, distribution and other characteristics of precipitates were determined.en
dc.publisherSavez inženjera metalurgije Srbije, Beograd
dc.rightsopenAccess
dc.sourceMetalurgija
dc.subjectcontinuous heatingen
dc.subjectprecipitationen
dc.subjectmorphologyen
dc.subjectstrengthening phasesen
dc.titleEffect of heating rate on precipitation of peak-aged Al-Li (8091) alloy: A quantitative approachen
dc.typearticle
dc.rights.licenseARR
dc.citation.epage45
dc.citation.issue1
dc.citation.other16(1): 39-45
dc.citation.rankM24
dc.citation.spage39
dc.citation.volume16
dc.identifier.rcubhttps://hdl.handle.net/21.15107/rcub_technorep_1588
dc.type.versionpublishedVersion


Документи

ДатотекеВеличинаФорматПреглед

Уз овај запис нема датотека.

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу