Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method

Jokić, Bojan; Drmanić, Saša; Radetić, Tamara; Krstić, Jugoslav; Petrović, Rada; Orlović, Aleksandar; Janaćković, Đorđe

doi:10.1016/j.matlet.2010.06.066

Samo za registrovane korisnike

2010

Autori

Jokić, Bojan
Drmanić, Saša

Petrović, Rada

Članak u časopisu (Objavljena verzija)

Metapodaci

Prikaz svih podataka o dokumentu

Apstrakt

Submicron carbon spherical particles were obtained by polycondensation of resorcinol and formaldehyde in a solution and subsequent ultrasonic spray pyrolysis of the prepared sol. Microscopic characterization indicates the regular spherical shape of the obtained particles and sphere diameters in 200-700 nm range. The carbon spheres are amorphous as confirmed by electron diffraction, EELS, XRD and HREM characterization. Activation procedure was performed with H2O in a nitrogen flow for 15 and 30 min at 800 degrees C. The activation procedure preserved the initial spherical shapes of the particles while the particle porosity and specific surface area were increased. The amount of surface oxygen functionalities was also increased by activation procedure as indicated by FTIR analysis.

Ključne reči:

Powder technology / Porosity / Nanomaterials

Izvor:
Materials Letters, 2010, 64, 20, 2173-2176

Izdavač:

Elsevier, Amsterdam

Finansiranje / projekti:

Sinteza, struktura, svojstva i primena funkcionalnih nanostrukturnih keramičkih i biokeramičkih materijala (RS-142070)
Office of Science, Office of Basic Energy Sciences, of the U.S. Department of EnergyUnited States Department of Energy (DOE) [DE-AC02-05CH11231]

DOI: 10.1016/j.matlet.2010.06.066

ISSN: 0167-577X

WoS: 000281997900009

Scopus: 2-s2.0-77955079994

[ Google Scholar ]


	10
	8

TY  - JOUR
AU  - Jokić, Bojan
AU  - Drmanić, Saša
AU  - Radetić, Tamara
AU  - Krstić, Jugoslav
AU  - Petrović, Rada
AU  - Orlović, Aleksandar
AU  - Janaćković, Đorđe
PY  - 2010
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1661
AB  - Submicron carbon spherical particles were obtained by polycondensation of resorcinol and formaldehyde in a solution and subsequent ultrasonic spray pyrolysis of the prepared sol. Microscopic characterization indicates the regular spherical shape of the obtained particles and sphere diameters in 200-700 nm range. The carbon spheres are amorphous as confirmed by electron diffraction, EELS, XRD and HREM characterization. Activation procedure was performed with H2O in a nitrogen flow for 15 and 30 min at 800 degrees C. The activation procedure preserved the initial spherical shapes of the particles while the particle porosity and specific surface area were increased. The amount of surface oxygen functionalities was also increased by activation procedure as indicated by FTIR analysis.
PB  - Elsevier, Amsterdam
T2  - Materials Letters
T1  - Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method
EP  - 2176
IS  - 20
SP  - 2173
VL  - 64
DO  - 10.1016/j.matlet.2010.06.066
ER  -

@article{
author = "Jokić, Bojan and Drmanić, Saša and Radetić, Tamara and Krstić, Jugoslav and Petrović, Rada and Orlović, Aleksandar and Janaćković, Đorđe",
year = "2010",
abstract = "Submicron carbon spherical particles were obtained by polycondensation of resorcinol and formaldehyde in a solution and subsequent ultrasonic spray pyrolysis of the prepared sol. Microscopic characterization indicates the regular spherical shape of the obtained particles and sphere diameters in 200-700 nm range. The carbon spheres are amorphous as confirmed by electron diffraction, EELS, XRD and HREM characterization. Activation procedure was performed with H2O in a nitrogen flow for 15 and 30 min at 800 degrees C. The activation procedure preserved the initial spherical shapes of the particles while the particle porosity and specific surface area were increased. The amount of surface oxygen functionalities was also increased by activation procedure as indicated by FTIR analysis.",
publisher = "Elsevier, Amsterdam",
journal = "Materials Letters",
title = "Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method",
pages = "2176-2173",
number = "20",
volume = "64",
doi = "10.1016/j.matlet.2010.06.066"
}

Jokić, B., Drmanić, S., Radetić, T., Krstić, J., Petrović, R., Orlović, A.,& Janaćković, Đ.. (2010). Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method. in Materials Letters
Elsevier, Amsterdam., 64(20), 2173-2176.
https://doi.org/10.1016/j.matlet.2010.06.066

Jokić B, Drmanić S, Radetić T, Krstić J, Petrović R, Orlović A, Janaćković Đ. Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method. in Materials Letters. 2010;64(20):2173-2176.
doi:10.1016/j.matlet.2010.06.066 .

Jokić, Bojan, Drmanić, Saša, Radetić, Tamara, Krstić, Jugoslav, Petrović, Rada, Orlović, Aleksandar, Janaćković, Đorđe, "Synthesis of submicron carbon spheres by the ultrasonic spray pyrolysis method" in Materials Letters, 64, no. 20 (2010):2173-2176,
https://doi.org/10.1016/j.matlet.2010.06.066 . .