dc.description.abstractExperimental results indicate that vanadium affects the solidification process in high chromium iron. Vanadium is distributed between eutectic M7C3 carbide and the matrix, but its content in carbide is considerably higher. Also, this element forms vanadium carbide. TEM observation reveals that vanadium carbide present in examined Fe-Cr-C-V alloys is being of M6C5 type. DTA analysis found that with increasing vanadium content in tested alloys, liquidus temperature is decreasing, while eutectic temperature is increasing, i.e. the solidification temperature interval reduces. The narrowing of the solidification temperature interval and the formation of larger amount of vanadium carbides, as a result of the increase in the vanadium content of the alloy, will favour the appearance of a finer structure. In addition, the phases volume fraction will change. i.e. the primary gamma-phase fraction will decrease and the amount of M7C3 carbide will increase. [doi:10.2320/matertrans.M2010059]en
dc.publisherJapan Inst Metals, Sendai
dc.rightsopenAccess
dc.sourceMaterials Transactions
dc.subjectvanadium rich carbideen
dc.subjectliqudus temperatureen
dc.subjecteutectic temperatureen
dc.subjectsolidification temperature intervalen
dc.subjectiron-chromium-carbon-vanadium alloysen
dc.titleSolidification of High Chromium White Cast Iron Alloyed with Vanadiumen
dc.typearticle
dc.rights.licenseARR
dc.citation.epage390
dc.citation.issue3
dc.citation.other52(3): 386-390
dc.citation.rankM22
dc.citation.spage386
dc.citation.volume52
dc.identifier.doi10.2320/matertrans.M2010059
dc.identifier.fulltexthttp://TechnoRep.tmf.bg.ac.rs/bitstream/id/8684/52_386.pdf
dc.identifier.scopus2-s2.0-79955764434
dc.identifier.wos000290461000023
dc.type.versionpublishedVersion


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу