Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
The effect of heat treatment on toughness and wear resistance of Fe-Cr-C-Nb alloys / Uticaj termičke obrade na žilavost i otpornost na habanje Fe-Cr-C-Nb legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Alloying with niobium improves the mechanical properties of the high chromium irons. The alloy containing appriximately 3 %Nb gives the best compromise between wear resistance and toughness. These properties were improved ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Cavitation damages morphology of high-strength low-alloy steel
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
The influence of thermomechanical treatment and chemical composition on recrystallization of Al-Mg alloys
(Savez inženjera metalurgije Srbije, Beograd, 2007)
Recrystallization behaviour of AlMg3, AlMg4.5Mn and AlMg6Mn alloy plates subjected to different thermomechanical treatments (TMTs), has been studied by means of optical microscopy and hardness measurements. Applied two-stage ...
Application of instrumental methods in the investigation of properties and microstructure of construction concretes / Primena instrumentalnih metoda za ispitivanje svojstava i mikrostrukture konstukcionih betona
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Methods for the investigation of microstructure of construction concretes are presented in this paper. Concrete is a composite material, thus its microstructure consists of bonding agent (cement) and aggregate with predefined ...
Effect of heating rate on precipitation of peak-aged Al-Li (8091) alloy: A quantitative approach
(Savez inženjera metalurgije Srbije, Beograd, 2010)
Samples of Al-Li (8091) alloy were solution treated at 540ºC for 30 min, water-quenched and continuously heated in oil at 0.05 and 0.1ºC/min rates, from room temperature to 190ºC when the peak hardness was achieved. Having ...