Service life test of non-noble metal composite cathodes for hydrogen evolution in sodium hydroxide solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
In this work polarization characteristics and "service life" test of the non-noble metal composite coatings Ni-MoOx and Ni-MoO2 for hydrogen evolution reaction (HER) in 32 wt.% NaOH at 90 degrees C were investigated and ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Incorporation of Pt, Ru and Pt-Ru nanoparticles into ordered mesoporous carbons for efficient oxygen reduction reaction in alkaline media
(Electrochimica Acta, 2015)
Ordered mesoporous carbon, volume-doped up to 3w.% with Pt, Ru and Pt-Ru nanoparticles was synthesized by evaporation-induced self-assembly method, under acidic conditions. The content of incorporated metal was determined ...
Coupling electrokinetic with a cork-based permeable reactive barrier to prevent groundwater pollution: A case study on hexavalent chromium-contaminated soil
(Elsevier Ltd., 2022)
This work proposes an eco-efficient treatment technology for the remediation of a kaolinite-based clay soil artificially contaminated with hexavalent chromium (50 mg Cr(VI) kg–1 soil), combining electrokinetics (EK) with ...
Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
HCOOH oxidation on thin Pd layers on Au: Self-poisoning by the subsequent reaction of the reaction product
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The oxidation of HCOOH has been investigated on thin Pd layers ranging from 1 to 17 ML equivalents electrodeposited on polycrystalline Au substrate (Pd"Au). The results are compared to those on Pd black. Potentiodynamic ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...