Effect of heating rate on precipitation of peak-aged Al-Li (8091) alloy: A quantitative approach
(Savez inženjera metalurgije Srbije, Beograd, 2010)
Samples of Al-Li (8091) alloy were solution treated at 540ºC for 30 min, water-quenched and continuously heated in oil at 0.05 and 0.1ºC/min rates, from room temperature to 190ºC when the peak hardness was achieved. Having ...
The effects of thermomechanical treatment on the SCC resistance of highly alloyed Al-Mg sheet / Uticaj termomehaničke obrade na otpornost prema naponskoj koroziji visoko legiranih Al-Mg limova
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The effects of cold work and different heat treatments on the stress corrosion cracking (SCC) behavior of Al-Mg6.8% alloy were studied using slow strain rate testing (SSRT). The results have indicated high SCC susceptibility ...
Possibility of secondary lead slag stabilization in concrete with presence of selected additives
(Savez inženjera metalurgije Srbije, Beograd, 2010)
A comparative technical and environmental evaluation of products arising from the stabilization/solidification of secondary lead metallurgical slag into a cement matrix was performed. Provided samples of an industrial slag ...
Experimental design approach regarding kinetics of high pressure leaching processes / Dizajniranje eksperimenata u pogledu na kinetiku luženja pri visokim pritiscima
(Savez inženjera metalurgije Srbije, Beograd, 2003)
Kinetics of high pressure leaching of nickel latente ore "Rudjinci", Serbia was studied in this work. The following parameters: temperature, acid to ore ratio, stirring speed, and time were optimized in order to obtain the ...
Influence of Cr, Mn and Mo on structure and properties of V microalloyed medium carbon forging steels
(Savez inženjera metalurgije Srbije, Beograd, 2010)
The influence of Cr, Mo and Mn on microstructure and mechanical properties of V-microalloyed medium-carbon steels has been studied by means of metallography and mechanical testing. Cr, Mn and Mo addition promotes the ...
Laboratory investigation of cavitation resistance of materials: Modified ultrasonically induced cavitation test method / Laboratorijsko istraživanje kavitacione otpornosti materijala - modificirana ultrazvučna metoda
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Cavitation erosion represents an actual problem in machines, whose components such as propellers, blades of hydraulic pumps and turbines, are exposed to high-speed flow of liquid. Research exhibited that hydraulic machinery ...
Structure and kinetics of internal oxidation in Ag-Sn alloys / Struktura i kinetika interne oksidacije Ag-Sn legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Internal oxidation in Ag-Sn-In-Te and Ag-Sn-Cu-Bi alloys was tested. micro structures of casted and homogenized samples, as well as after internal oxidation were followed by optical microscopy. The structure of Ag-Sn-Cu-Bi ...
The influence of the solidification rate on the interface shape and distribution of solute
(Savez inženjera metalurgije Srbije, Beograd, 2002)
In this paper investigation of the influence of the solidification conditions on the interface shape and distribution of solute during the solidification of AI-Cu alloy by vertical Bridgman method were investigated. The ...
Approximation of material behaviour of PLLA polymer in HAp/PLLA biocomposite material using nanoindentation and finite element method
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In this work, a combination of nanoindentation experiment and finite element modeling is proposed in order to obtain approximate material behavior of PLLA polymer in hydroxyapatite (HAp)/poly-L-lactide (PLLA) composite. ...
Rotating disk alumina precursor fiber formation process stability determination using image analysis
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Precursor fibers are made from the aluminium-hydroxide chloride based sols. The process stability can be influenced both by the fiber formation conditions and the rheology of the sol. The distance from the disk canter is ...