Hydrometallurgical process for extraction of metals from electronic waste, Part I: Material characterization and process option selection
(Savez inženjera metalurgije Srbije, Beograd, 2009)
Used electronic equipment became one of the fastest growing waste streams in the world. In the past two decades recycling of printed circuit boards (PCBs) has been based on pyrometallurgy, highly polluting recycling ...
Synthesis and sintering of Cu-Al2O3 nanocomposite powders produced by a thermochemical route
(Savez inženjera metalurgije Srbije, Beograd, 2007)
By hydrometallurgy and powder metallurgy along with prognosis of physical-chemical properties, a synthesis of new improved materials can be successfully performed with in advance pre-set properties which is conditioned by ...
Determination of AL2O3particle size in Cu-AL2O3 nanocomposite materials using UV spectrophotometry / Određivanje veličine čestica AL2O3 u nanokompozitnim materijalima iz sistema Cu-AL2O3 primenom UV spektrofotometrije
(Savez inženjera metalurgije Srbije, Beograd, 2008)
In order to achieve improved mechanical properties of dispersion strengthened nanocomposite, without influencing electrical and thermal conductivity it is necessary for dispersoide to be nano sized and uniformly distributed ...
Characterization of nano-powder morphology obtained by ultrasonic spray pyrolysis
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Spherical nanosized particles of copper were synthesized by ultrasonic dispersion of solutions from copper sulphate in the temperature range of 800-900°C in hydrogen atmosphere. A controlled particle size was realized ...
Influence of milling parameters on the preparation of fine tungsten and copper powders by mechanically induced self-propagating reaction / Uticaj parametara mlevenja na dobijanje finih prahova volframa i bakra mehanički iniciranom samorasprostirućom reakcijom
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Mechanically induced self-propagating reaction in planetary ball mill was realized in three different systems, CaWO4 (scheelite) + Mg, CuO + Ti and CuO + Zr. An influence of a ball diameter (from 5 to 41.2 mm) at three ...