Now showing items 1-10 of 58
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
The effect of heat treatment on toughness and wear resistance of Fe-Cr-C-Nb alloys / Uticaj termičke obrade na žilavost i otpornost na habanje Fe-Cr-C-Nb legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Alloying with niobium improves the mechanical properties of the high chromium irons. The alloy containing appriximately 3 %Nb gives the best compromise between wear resistance and toughness. These properties were improved ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
A model for predicting fracture toughness in overaged 7000 alloy forgings
(Savez inženjera metalurgije Srbije, Beograd, 2007)
An attempt to develop a multiple micromechanism-based model for predicting plane-strain fracture toughness, KIc, of overaged 7000 alloy forgings has been made. The proposed model reveals the quantitative relations between ...
The influence of thermomechanical treatment on recrystallization of AlMg4.5Cu0.5 alloy
(Savez inženjera metalurgije Srbije, Beograd, 2007)
Recrystallization behavior of an Al-Mg-Cu alloy (4.5 wt. %Mg and 0.45 wt %Cu) subjected to different thermomechanical treatments (TMTs) have been studied by means of light optical microscopy and hardness measurements. In ...
Dynamic recrystallization in M2 tool steel during friction welding
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Friction welding of M2 tool steel and 1730 quenched and tempered steel was performed with the aim to reveal the origin of extremely fine martensitic grain in M2 steel after welding. Taking into account thermomechanical ...
Optimisation of ferriferous dust and mud preparation acts from iron and steel production on purpose of returning to primary processes / Optimizacija postupaka pripreme železonosnih prašina i muljeva iz proizvodnje gvožđa i čelika u cilju vraćanja u primarne procese
(Savez inženjera metalurgije Srbije, Beograd, 2004)
In this paper detailed characterization of ferriferous dust and mud which originated from aglomerization, blast- furnace and converter process in Iron-works Smederevo were shown. Optimization of method peletization was ...
Experimental and numerical evaluation of a steamline behaviour using local approach
(Croatian Metallurgical Society, 2007)
Results of the experimental and numerical comparative analysis of steamline pipes have been presented. New pipes and the pipes used for more than 117,000 hours at 540 degrees C under pressure of 42 bars have been simultaneously ...
The recycling of high magnesium aluminum alloys estimation of the most reliable procedure
(Savez inženjera metalurgije Srbije, Beograd, 2009)
Aluminum is one of the most recyclable materials. Namely, the properties of aluminum are not affected by the recycling and reuse, thus enable that high value of the metal is maintained after reprocessing. The re-smelting ...
Fuel consumption analysis in cooper melting and refining plants / Analiza potrošnje energenata u pogonima za topljenje i rafinaciju bakra
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Cathode cooper production and refining include significant consumption of almost all-conventional fuel types. The given consumption is high in specific and in nominal way. Especially high fuel value content is on Cathode ...