Impact of roughness of Zn-Mn coatings on corrosive stability / Uticaj hrapavosti Zn-Mn prevlaka na korozionu postojanost
(Engineering Society for Corrosion, Belgrade, Serbia, 2015)
This paper involves electrochemical deposition of Zn-Mn coatings from four solutions. We measured their roughness and corrosion stability. We used cathodes made of steel of unknown composition that were licensed under the ...
The characterization of ternary Zn-Ni-Co alloy coatings electrochemically deposited on steel from sulfate solution / Karakterizacija prevlaka trojnih legura Zn-Ni-Co na čeliku elektrolitički taloženih iz sulfatnog rastvora
(Engineering Society for Corrosion, Belgrade, Serbia, 2016)
In this work the electrochemical deposition of ternary Zn-Ni-Co alloy coatings on steel from sulfate, additive-free electrolyte, was investigated. The ratio of metal cations [Co2+]/[Ni2+] in the plating solution was analysed, ...
The comparative study of the corrosion stability of Zn-Ni-Co alloy coatings deposited from chloride and sulphate baths / Uporedna analiza korozione stabilnosti prevlaka Zn-Ni-Co legura elektrohemijski taloženih iz hloridnih i sulfatnih rastvora
(Engineering Society for Corrosion, Belgrade, Serbia, 2017)
The ternary Zn-Ni-Co alloy coatings were electrodeposited on steel from chloride and sulphate baths. The deposition was carried out galvanostatically at different current densities at ambient temperatures from additives ...
Tailoring the corrosion resistance of Zn-Mn coating by electrodeposition from deep eutectic solvents / Poboljšanje korozione postojanosti Zn-Mn prevlake, elektrohemijskim taloženjem iz dubokih eutektičkih smeša
(Engineering Society for Corrosion, Belgrade, Serbia, 2018)
Well adhered, homogenous coatings were obtained from deep eutectic solvents (DES) based on choline chloride and urea, at current densities up to 20 mA cm-2. The coatings' morphology was analyzed by atomic force microscopy, ...