The effect of T4 heat treatment on the microstructure and corrosion behaviour of Zn27Al1.5Cu0.02Mg alloy
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
The effect of heat treatment on the microstructure and corrosion behaviour of Zn27Al1 5CuO 02Mg alloy was examined The alloy was prepared by melting and casting route and then thermally processed (T4 regime) Corrosion ...
Composition and processing effects on the electrochemical characteristics of biomedical titanium alloys
(Pergamon-Elsevier Science Ltd, Oxford, 2014)
The electrochemical behaviour of the Ti-13Nb-13Zr and Ti-6Al-4V ELI alloys with martensitic microstructures was investigated by polarization and electrochemical impedance spectroscopy (EIS) in Ringer's solution. The impedance ...
Microstructure and pitting corrosion resistance of annealed duplex stainless steel
(Elsevier Ltd, 2006)
The transition from metastable to stable pitting was studied in 0.5 M NaCl water solution for two cast duplex stainless steels under different microstructural conditions achieved by annealing in the range from 900 °C to ...
Wear and corrosion behaviour of Ti-13Nb-13Zr and Ti-6Al-4V alloys in simulated physiological solution
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Wear and corrosion behaviour of cold-rolled Ti-13Nb-13Zr alloy, with martensitic microstructure, and Ti-6Al-4V ELI alloy, in martensitic and two-phase (alpha + beta) microstructural conditions, was studied in a Ringer's ...
Adsorption and corrosion inhibitive properties of some organic molecules on iron electrode in sulfuric acid
(Elsevier, 2002)
Adsorption and corrosion inhibitive properties of three different organic molecules: 2-naphthalenesulfonic acid, 2,7-naphthalenedisulfonic acid and 2-naphthol-3,6-disulfonic acid are investigated on Armco-iron electrode ...
Electrochemical testing of noble metal dental alloys: The influence of their chemical composition on the corrosion resistance
(Corrosion Science, 2021)
Platinum and nine commercial dental alloys with the contents of noble metals ranging from 27 wt.% to 97.6 wt. % were investigated by the procedure described in the Standard ISO 10271:2009, Electrochemical testing was ...
Corrosion stability of epoxy coatings on aluminum pretreated by vinyltriethoxysilane
(Pergamon-Elsevier Science Ltd, Oxford, 2008)
The electrochemical and transport properties and adhesion of epoxy coatings electrodeposited on aluminum pretreated by vinyltriethoxysilane (VTES) were investigated during exposure to 3% NaCl. The VTES films were deposited ...
Oxygen reduction on a duplex stainless steel
(Pergamon-Elsevier Science Ltd, Oxford, 1998)
O-2 reduction on duplex stainless steel was investigated in neutral and alkaline solutions with and without the presence of chloride ions. All polarization curves showed hysteresis with higher reaction rate in positive ...
Corrosion protection of aluminium pretreated by vinyltriethoxysilane in sodium chloride solution
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The corrosion protection of vinyltriethoxysilane (VTES) films on aluminium during exposure to 3% NaCl was investigated using electrochemical impedance spectroscopy (EIS), potential-time measurements and optical microscopy ...
Initial corrosion protection of Zn-Mn alloys electrodeposited from alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
The effects of a deposition current density (c.d.) on the corrosion behaviour of Zn-Mn alloy coatings, deposited from alkaline pyrophosphate solution, were investigated by atomic absorption spectrophotometry (AAS), X-ray ...