Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Thermodynamic and structural investigation of the Ag-In-Sb system
(Croatian Metallurgical Society, 2007)
The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented ...
Laboratory investigation of cavitation resistance of materials: Modified ultrasonically induced cavitation test method / Laboratorijsko istraživanje kavitacione otpornosti materijala - modificirana ultrazvučna metoda
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Cavitation erosion represents an actual problem in machines, whose components such as propellers, blades of hydraulic pumps and turbines, are exposed to high-speed flow of liquid. Research exhibited that hydraulic machinery ...
Approximation of material behaviour of PLLA polymer in HAp/PLLA biocomposite material using nanoindentation and finite element method
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In this work, a combination of nanoindentation experiment and finite element modeling is proposed in order to obtain approximate material behavior of PLLA polymer in hydroxyapatite (HAp)/poly-L-lactide (PLLA) composite. ...
Rotating disk alumina precursor fiber formation process stability determination using image analysis
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Precursor fibers are made from the aluminium-hydroxide chloride based sols. The process stability can be influenced both by the fiber formation conditions and the rheology of the sol. The distance from the disk canter is ...