The goal of this study was to prepare a CaO·ZnO catalyst containing a small amount of K2CO3 and analyze its activity for biodiesel synthesis. The catalyst was prepared using the following procedure: CaO and ZnO (mole ratio of 1:2), water and K2CO3 (in various amounts) were mechanochemically treated and after milling heated at 700°C in air atmosphere for obtaining mixed CaO·ZnO/xK2CO3 oxides (x = 0, 1, 2 and 4 mol of K2CO3 per 10 mol of CaO). All the samples were characterized by X-ray diffraction (XRD), inductively coupled plasma (ICP), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning electron microscopy/ energy-dispersive spectroscopy (SEM/EDS), particle size laser diffraction (PSLD) distribution, solubility measurement of Ca, Zn and K ions in methanol as well as by determination of their alkalinity (Hammett indicator method). Prepared CaO·ZnO/xK2CO3 composite powders were tested as catalysts for methanolysis of sunflower... oil at 70 °C using mole ratio of sunflower oil to methanol of 1:10 and with 2 mass% of catalyst based on oil weight. The presence of K2CO3 in prepared samples was found to increase the activity of catalyst, and that such effect is caused by homogeneous-heterogeneous catalysis of biodiesel synthesis.
Cilj ovih istraživanja bio je da se pripremi CaO·ZnO katalizator koji sadrži malu količinu K2CO3 i analizira njegova aktivnost u sintezi biodizela. Katalizator je pripremljen prema sledećoj proceduri: CaO i ZnO (molski odnos 1:2), voda i K2CO3 (u različitoj količini) su tretirani mehanohemijski i nakon mlevenja zagrevani na 700 °C u atmosferi vazduha da bi se dobila smeša oksida CaO·ZnO/xK2CO3 (x = 0, 1, 2 i 4 mol K2CO3 na 10 mol CaO). Karakterizacija pripremljenih katalizatora izvršena je metodama rendgenske difrakcije (XRD), indukovane kuplovane plazme (ICP), spektroskopije fotoelektrona dobijenih X-zracima (XPS), termogravimetrijske analize (TGA), infracrvene spektroskopije (FTIR), skenirajuće elektronske mikroskopije i energetske disperzione spektroskopije (SEM/EDS), raspodele veličine čestica (PSLD), merenjem rastvorljivosti katalizatora odnosno Ca, Zn i K jona u metanolu, kao i određivanjem njihove baznosti (metodom Hametovih indikatora). Pripremljeni CaO·ZnO/xK2CO3 kompozitni pr...ahovi testirani su kao katalizatori u reakciji metanolize suncokretovog ulja na 70 °C, pri molarnom odnosu suncokretovog ulja i metanola od 1:10 i sa 2 mas.% katalizatora u odnosu na masu ulja. Pokazano je da prisustvo K2CO3 u pripremljenim uzorcima povećava aktivnost katalizatora i da je takav efekat posledica homogeno-heterogene katalize u sintezi biodizela.
TY - JOUR
AU - Kesić, Željka
AU - Lukić, Ivana
AU - Zdujić, Miodrag
AU - Jovalekić, Čedomir
AU - Liu, Hui
AU - Skala, Dejan
PY - 2015
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2921
AB - The goal of this study was to prepare a CaO·ZnO catalyst containing a small amount of K2CO3 and analyze its activity for biodiesel synthesis. The catalyst was prepared using the following procedure: CaO and ZnO (mole ratio of 1:2), water and K2CO3 (in various amounts) were mechanochemically treated and after milling heated at 700°C in air atmosphere for obtaining mixed CaO·ZnO/xK2CO3 oxides (x = 0, 1, 2 and 4 mol of K2CO3 per 10 mol of CaO). All the samples were characterized by X-ray diffraction (XRD), inductively coupled plasma (ICP), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning electron microscopy/ energy-dispersive spectroscopy (SEM/EDS), particle size laser diffraction (PSLD) distribution, solubility measurement of Ca, Zn and K ions in methanol as well as by determination of their alkalinity (Hammett indicator method). Prepared CaO·ZnO/xK2CO3 composite powders were tested as catalysts for methanolysis of sunflower oil at 70 °C using mole ratio of sunflower oil to methanol of 1:10 and with 2 mass% of catalyst based on oil weight. The presence of K2CO3 in prepared samples was found to increase the activity of catalyst, and that such effect is caused by homogeneous-heterogeneous catalysis of biodiesel synthesis.
AB - Cilj ovih istraživanja bio je da se pripremi CaO·ZnO katalizator koji sadrži malu količinu K2CO3 i analizira njegova aktivnost u sintezi biodizela. Katalizator je pripremljen prema sledećoj proceduri: CaO i ZnO (molski odnos 1:2), voda i K2CO3 (u različitoj količini) su tretirani mehanohemijski i nakon mlevenja zagrevani na 700 °C u atmosferi vazduha da bi se dobila smeša oksida CaO·ZnO/xK2CO3 (x = 0, 1, 2 i 4 mol K2CO3 na 10 mol CaO). Karakterizacija pripremljenih katalizatora izvršena je metodama rendgenske difrakcije (XRD), indukovane kuplovane plazme (ICP), spektroskopije fotoelektrona dobijenih X-zracima (XPS), termogravimetrijske analize (TGA), infracrvene spektroskopije (FTIR), skenirajuće elektronske mikroskopije i energetske disperzione spektroskopije (SEM/EDS), raspodele veličine čestica (PSLD), merenjem rastvorljivosti katalizatora odnosno Ca, Zn i K jona u metanolu, kao i određivanjem njihove baznosti (metodom Hametovih indikatora). Pripremljeni CaO·ZnO/xK2CO3 kompozitni prahovi testirani su kao katalizatori u reakciji metanolize suncokretovog ulja na 70 °C, pri molarnom odnosu suncokretovog ulja i metanola od 1:10 i sa 2 mas.% katalizatora u odnosu na masu ulja. Pokazano je da prisustvo K2CO3 u pripremljenim uzorcima povećava aktivnost katalizatora i da je takav efekat posledica homogeno-heterogene katalize u sintezi biodizela.
PB - Association of the Chemical Engineers of Serbia
T2 - Chemical Industry & Chemical Engineering Quarterly
T1 - Mechanochemical synthesis of CaO·ZnO.K2CO3 catalyst: Characterization and activity for methanolysis of sunflower oil
T1 - Mehanohemijska sinteza CaO·ZnO.K2CO3, katalizatora - karakterizacija i aktivnost u metanolizi suncokretovog ulja
EP - 12
IS - 1-1
SP - 1
VL - 21
DO - 10.2298/CICEQ131026041K
ER -
@article{
author = "Kesić, Željka and Lukić, Ivana and Zdujić, Miodrag and Jovalekić, Čedomir and Liu, Hui and Skala, Dejan",
year = "2015",
abstract = "The goal of this study was to prepare a CaO·ZnO catalyst containing a small amount of K2CO3 and analyze its activity for biodiesel synthesis. The catalyst was prepared using the following procedure: CaO and ZnO (mole ratio of 1:2), water and K2CO3 (in various amounts) were mechanochemically treated and after milling heated at 700°C in air atmosphere for obtaining mixed CaO·ZnO/xK2CO3 oxides (x = 0, 1, 2 and 4 mol of K2CO3 per 10 mol of CaO). All the samples were characterized by X-ray diffraction (XRD), inductively coupled plasma (ICP), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning electron microscopy/ energy-dispersive spectroscopy (SEM/EDS), particle size laser diffraction (PSLD) distribution, solubility measurement of Ca, Zn and K ions in methanol as well as by determination of their alkalinity (Hammett indicator method). Prepared CaO·ZnO/xK2CO3 composite powders were tested as catalysts for methanolysis of sunflower oil at 70 °C using mole ratio of sunflower oil to methanol of 1:10 and with 2 mass% of catalyst based on oil weight. The presence of K2CO3 in prepared samples was found to increase the activity of catalyst, and that such effect is caused by homogeneous-heterogeneous catalysis of biodiesel synthesis., Cilj ovih istraživanja bio je da se pripremi CaO·ZnO katalizator koji sadrži malu količinu K2CO3 i analizira njegova aktivnost u sintezi biodizela. Katalizator je pripremljen prema sledećoj proceduri: CaO i ZnO (molski odnos 1:2), voda i K2CO3 (u različitoj količini) su tretirani mehanohemijski i nakon mlevenja zagrevani na 700 °C u atmosferi vazduha da bi se dobila smeša oksida CaO·ZnO/xK2CO3 (x = 0, 1, 2 i 4 mol K2CO3 na 10 mol CaO). Karakterizacija pripremljenih katalizatora izvršena je metodama rendgenske difrakcije (XRD), indukovane kuplovane plazme (ICP), spektroskopije fotoelektrona dobijenih X-zracima (XPS), termogravimetrijske analize (TGA), infracrvene spektroskopije (FTIR), skenirajuće elektronske mikroskopije i energetske disperzione spektroskopije (SEM/EDS), raspodele veličine čestica (PSLD), merenjem rastvorljivosti katalizatora odnosno Ca, Zn i K jona u metanolu, kao i određivanjem njihove baznosti (metodom Hametovih indikatora). Pripremljeni CaO·ZnO/xK2CO3 kompozitni prahovi testirani su kao katalizatori u reakciji metanolize suncokretovog ulja na 70 °C, pri molarnom odnosu suncokretovog ulja i metanola od 1:10 i sa 2 mas.% katalizatora u odnosu na masu ulja. Pokazano je da prisustvo K2CO3 u pripremljenim uzorcima povećava aktivnost katalizatora i da je takav efekat posledica homogeno-heterogene katalize u sintezi biodizela.",
publisher = "Association of the Chemical Engineers of Serbia",
journal = "Chemical Industry & Chemical Engineering Quarterly",
title = "Mechanochemical synthesis of CaO·ZnO.K2CO3 catalyst: Characterization and activity for methanolysis of sunflower oil, Mehanohemijska sinteza CaO·ZnO.K2CO3, katalizatora - karakterizacija i aktivnost u metanolizi suncokretovog ulja",
pages = "12-1",
number = "1-1",
volume = "21",
doi = "10.2298/CICEQ131026041K"
}
Kesić, Ž., Lukić, I., Zdujić, M., Jovalekić, Č., Liu, H.,& Skala, D.. (2015). Mechanochemical synthesis of CaO·ZnO.K2CO3 catalyst: Characterization and activity for methanolysis of sunflower oil. in Chemical Industry & Chemical Engineering Quarterly
Association of the Chemical Engineers of Serbia., 21(1-1), 1-12.
https://doi.org/10.2298/CICEQ131026041K
Kesić Ž, Lukić I, Zdujić M, Jovalekić Č, Liu H, Skala D. Mechanochemical synthesis of CaO·ZnO.K2CO3 catalyst: Characterization and activity for methanolysis of sunflower oil. in Chemical Industry & Chemical Engineering Quarterly. 2015;21(1-1):1-12.
doi:10.2298/CICEQ131026041K .
Kesić, Željka, Lukić, Ivana, Zdujić, Miodrag, Jovalekić, Čedomir, Liu, Hui, Skala, Dejan, "Mechanochemical synthesis of CaO·ZnO.K2CO3 catalyst: Characterization and activity for methanolysis of sunflower oil" in Chemical Industry & Chemical Engineering Quarterly, 21, no. 1-1 (2015):1-12,
https://doi.org/10.2298/CICEQ131026041K . .