Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete
Abstract
Low level laser (LLL) was applied to induct destruction of the low cement high alumina refractory concrete (LCC) samples. Three different series of samples were used in the experiment: a reference one dried at 105 degrees C, sintered at 1300 degrees C and sintered at 1600 degrees C. Level of destruction during time interval from 5 to 25 min was monitored by measuring surface and depth of damage. Obtained results shown that minimal level of destruction was observed for the samples sinteted at 1600 degrees C for the whole time interval.
Keywords:
Low level laser (LLL) / Laser destruction / Mechanical comparator / Image analysis / Damages size / Refractory concreteSource:
Engineering Structures, 2015, 99, 462-467Publisher:
- Elsevier Sci Ltd, Oxford
Funding / projects:
DOI: 10.1016/j.engstruct.2015.05.020
ISSN: 0141-0296
WoS: 000359171900037
Scopus: 2-s2.0-84930209265
Institution/Community
Tehnološko-metalurški fakultetTY - JOUR AU - Martinović, Sanja AU - Vlahović, Milica AU - Stević, Zoran AU - Volkov-Husović, Tatjana PY - 2015 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3109 AB - Low level laser (LLL) was applied to induct destruction of the low cement high alumina refractory concrete (LCC) samples. Three different series of samples were used in the experiment: a reference one dried at 105 degrees C, sintered at 1300 degrees C and sintered at 1600 degrees C. Level of destruction during time interval from 5 to 25 min was monitored by measuring surface and depth of damage. Obtained results shown that minimal level of destruction was observed for the samples sinteted at 1600 degrees C for the whole time interval. PB - Elsevier Sci Ltd, Oxford T2 - Engineering Structures T1 - Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete EP - 467 SP - 462 VL - 99 DO - 10.1016/j.engstruct.2015.05.020 ER -
@article{ author = "Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Volkov-Husović, Tatjana", year = "2015", abstract = "Low level laser (LLL) was applied to induct destruction of the low cement high alumina refractory concrete (LCC) samples. Three different series of samples were used in the experiment: a reference one dried at 105 degrees C, sintered at 1300 degrees C and sintered at 1600 degrees C. Level of destruction during time interval from 5 to 25 min was monitored by measuring surface and depth of damage. Obtained results shown that minimal level of destruction was observed for the samples sinteted at 1600 degrees C for the whole time interval.", publisher = "Elsevier Sci Ltd, Oxford", journal = "Engineering Structures", title = "Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete", pages = "467-462", volume = "99", doi = "10.1016/j.engstruct.2015.05.020" }
Martinović, S., Vlahović, M., Stević, Z.,& Volkov-Husović, T.. (2015). Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete. in Engineering Structures Elsevier Sci Ltd, Oxford., 99, 462-467. https://doi.org/10.1016/j.engstruct.2015.05.020
Martinović S, Vlahović M, Stević Z, Volkov-Husović T. Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete. in Engineering Structures. 2015;99:462-467. doi:10.1016/j.engstruct.2015.05.020 .
Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Volkov-Husović, Tatjana, "Influence of sintering temperature on low level laser (LLL) destruction of low cement high alumina refractory concrete" in Engineering Structures, 99 (2015):462-467, https://doi.org/10.1016/j.engstruct.2015.05.020 . .