Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn
Samo za registrovane korisnike
2016
Poglavlje u monografiji (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Microstructural changes of DC-cast 5xxx series AI-Mg-Mn alloy modified with Zn addition occurring during the homogenization treatments were studied through the thickness of a rolling ingot. The homogenization treatments included: low temperature annealing at 430 degrees C for 12h and high temperature homogenization at 550 degrees C for 16h. Microstructure evolution was followed by electrical resistivity measurements, optical microscopy, SEM and TEM characterization and microanalysis. During the homogenization, decomposition of the supersaturated solid solution, present in the as-cast state, occurred. Distribution of the precipitates was dictated by segregations and could be related to the partition coefficients of alloying elements. It was found that during the high temperature homogenization not only dissolution processes occurred, but also precipitation of new phases.
Ključne reči:
Al-Mg alloy / Al-6(Mn,Fe) / Al10Mn / homogenizationIzvor:
Light Metals 2012, 2016, 387-392Finansiranje / projekti:
DOI: 10.1007/978-3-319-48179-1_65
ISBN: 978-331948179-1
PubMed:
WoS: 000324538600065
Scopus: 2-s2.0-85015838311
Institucija/grupa
Tehnološko-metalurški fakultetTY - CHAP AU - Halap, Akram AU - Radetić, Tamara AU - Popović, Miljana AU - Romhanji, Endre PY - 2016 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3169 AB - Microstructural changes of DC-cast 5xxx series AI-Mg-Mn alloy modified with Zn addition occurring during the homogenization treatments were studied through the thickness of a rolling ingot. The homogenization treatments included: low temperature annealing at 430 degrees C for 12h and high temperature homogenization at 550 degrees C for 16h. Microstructure evolution was followed by electrical resistivity measurements, optical microscopy, SEM and TEM characterization and microanalysis. During the homogenization, decomposition of the supersaturated solid solution, present in the as-cast state, occurred. Distribution of the precipitates was dictated by segregations and could be related to the partition coefficients of alloying elements. It was found that during the high temperature homogenization not only dissolution processes occurred, but also precipitation of new phases. T2 - Light Metals 2012 T1 - Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn EP - 392 SP - 387 DO - 10.1007/978-3-319-48179-1_65 ER -
@inbook{ author = "Halap, Akram and Radetić, Tamara and Popović, Miljana and Romhanji, Endre", year = "2016", abstract = "Microstructural changes of DC-cast 5xxx series AI-Mg-Mn alloy modified with Zn addition occurring during the homogenization treatments were studied through the thickness of a rolling ingot. The homogenization treatments included: low temperature annealing at 430 degrees C for 12h and high temperature homogenization at 550 degrees C for 16h. Microstructure evolution was followed by electrical resistivity measurements, optical microscopy, SEM and TEM characterization and microanalysis. During the homogenization, decomposition of the supersaturated solid solution, present in the as-cast state, occurred. Distribution of the precipitates was dictated by segregations and could be related to the partition coefficients of alloying elements. It was found that during the high temperature homogenization not only dissolution processes occurred, but also precipitation of new phases.", journal = "Light Metals 2012", booktitle = "Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn", pages = "392-387", doi = "10.1007/978-3-319-48179-1_65" }
Halap, A., Radetić, T., Popović, M.,& Romhanji, E.. (2016). Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn. in Light Metals 2012, 387-392. https://doi.org/10.1007/978-3-319-48179-1_65
Halap A, Radetić T, Popović M, Romhanji E. Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn. in Light Metals 2012. 2016;:387-392. doi:10.1007/978-3-319-48179-1_65 .
Halap, Akram, Radetić, Tamara, Popović, Miljana, Romhanji, Endre, "Study of homogenization treatments of cast 5xxx series ai-mg-mn alloy modified with zn" in Light Metals 2012 (2016):387-392, https://doi.org/10.1007/978-3-319-48179-1_65 . .