Healing efficiency of polystyrene electrospun nanofibers with Grubbs' catalyst in thermosetting composite

Abstract

The study presents a novel method for the protection of Grubbs' catalyst, by incorporation in polystyrene fibres via electrospinning technique. Epoxy-glass fibre composite with embedded self-healing agents (polystyrene fibres with Grubbs' and microcapsules with dicyclopentadiene) was processed. Fibres retained pale purple colour during processing, revealing that fibres provided good protection of the catalyst from the amine hardener. The influence of self-healing agents' content and thermal treatment on self-healing efficiency was investigated. Fourier transform infrared spectroscopy revealed that a polydicyclopentadiene formed at the healed interface. Thermal analysis revealed that bleed' at the healing sites from different samples had similar concentration of polydicyclopentadiene, indicating that the same amount of the catalyst has been provided to dicyclopentadiene for polymerization. This finding lead to assumption that electrospun polymer fibres enabled good dispersion of the catalyst in the composites. The low energy impact tests of the samples showed a recovery of 90% after 24h at room temperature and up to 111% after repeated heating cycles.