TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M (NH4)(2)SO4 solution in a temperature-controlled bath. The pH values of the suspension were 7, 8 or 9. According to the x-ray diffraction (XRD) analysis the anatase crystallite sizes were about 12 nm, which coincided with the average particle size revealed by scanning electron microscopy (SEM). The Raman scattering measurements have shown the presence of a small amount of highly disordered brookite phase in addition to dominant anatase phase with similar nanostructure in all synthesized powders. BET measurements revealed that all synthesized catalysts were fully mesoporous, except the sample synthesized with 0.07 M (NH4)(2)SO4 at pH=9, which had small amount of micropores. The photocatalytic degradation of herbicide Clomazone was carried out for both the pure active subs...tance and as the commercial product (GAMIT 4-EC) under UV irradiation. The best photocatalytic efficiency was obtained for the catalyst with the largest specific surface area, confirming this parameter as crucial for enhanced photocatalytic degradation of the pure active substance and commercial product of herbicide Clomazone.
TY - JOUR
AU - Golubović, Aleksandar
AU - Simović, Bojana
AU - Gašić, Slavica
AU - Mijin, Dušan
AU - Matković, Aleksandar
AU - Babić, Biljana M.
AU - Scepanović, Maja
PY - 2017
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3628
AB - TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M (NH4)(2)SO4 solution in a temperature-controlled bath. The pH values of the suspension were 7, 8 or 9. According to the x-ray diffraction (XRD) analysis the anatase crystallite sizes were about 12 nm, which coincided with the average particle size revealed by scanning electron microscopy (SEM). The Raman scattering measurements have shown the presence of a small amount of highly disordered brookite phase in addition to dominant anatase phase with similar nanostructure in all synthesized powders. BET measurements revealed that all synthesized catalysts were fully mesoporous, except the sample synthesized with 0.07 M (NH4)(2)SO4 at pH=9, which had small amount of micropores. The photocatalytic degradation of herbicide Clomazone was carried out for both the pure active substance and as the commercial product (GAMIT 4-EC) under UV irradiation. The best photocatalytic efficiency was obtained for the catalyst with the largest specific surface area, confirming this parameter as crucial for enhanced photocatalytic degradation of the pure active substance and commercial product of herbicide Clomazone.
PB - Međunarodni Institut za nauku o sinterovanju, Beograd
T2 - Science of Sintering
T1 - Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media
EP - 330
IS - 3
SP - 319
VL - 49
DO - 10.2298/SOS1703319G
ER -
@article{
author = "Golubović, Aleksandar and Simović, Bojana and Gašić, Slavica and Mijin, Dušan and Matković, Aleksandar and Babić, Biljana M. and Scepanović, Maja",
year = "2017",
abstract = "TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M (NH4)(2)SO4 solution in a temperature-controlled bath. The pH values of the suspension were 7, 8 or 9. According to the x-ray diffraction (XRD) analysis the anatase crystallite sizes were about 12 nm, which coincided with the average particle size revealed by scanning electron microscopy (SEM). The Raman scattering measurements have shown the presence of a small amount of highly disordered brookite phase in addition to dominant anatase phase with similar nanostructure in all synthesized powders. BET measurements revealed that all synthesized catalysts were fully mesoporous, except the sample synthesized with 0.07 M (NH4)(2)SO4 at pH=9, which had small amount of micropores. The photocatalytic degradation of herbicide Clomazone was carried out for both the pure active substance and as the commercial product (GAMIT 4-EC) under UV irradiation. The best photocatalytic efficiency was obtained for the catalyst with the largest specific surface area, confirming this parameter as crucial for enhanced photocatalytic degradation of the pure active substance and commercial product of herbicide Clomazone.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media",
pages = "330-319",
number = "3",
volume = "49",
doi = "10.2298/SOS1703319G"
}
Golubović, A., Simović, B., Gašić, S., Mijin, D., Matković, A., Babić, B. M.,& Scepanović, M.. (2017). Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 49(3), 319-330.
https://doi.org/10.2298/SOS1703319G
Golubović A, Simović B, Gašić S, Mijin D, Matković A, Babić BM, Scepanović M. Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media. in Science of Sintering. 2017;49(3):319-330.
doi:10.2298/SOS1703319G .
Golubović, Aleksandar, Simović, Bojana, Gašić, Slavica, Mijin, Dušan, Matković, Aleksandar, Babić, Biljana M., Scepanović, Maja, "Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media" in Science of Sintering, 49, no. 3 (2017):319-330,
https://doi.org/10.2298/SOS1703319G . .