Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem
Mechanical properties of UHMWPE/EVA hybrid composite reinforced with fibers obtained by electrospinning
Authors
Zec, JelenaTomić, Nataša
Vuksanović, Marija M.
Veljović, Đorđe
Stojanović, Dušica
Jančić-Heinemann, Radmila
Article (Published version)
Metadata
Show full item recordAbstract
Aluminijum oksidna (Al2O3) nanovlakna pripremljena su iz vodenog rastvora aluminijum hlorohidrata/poli(vinil alkohola) (PVA) korišćenjem tehnike elektropredenja. Maseni odnos aluminijum hlorohidrata/PVA bio je 5:1. Nakon kalcinacije vlakana na 1100 °C, dobijena su kratka aluminijum oksidna vlakna prečnika od 200 do 800 nm. Morfologija vlakana je karakterisana pomoću skenirajućeg elektronskog mikroskopa sa emisijom polja (FE-SEM). Softver za analizu slike Image ProPlus korišćen je za merenje prečnika dobijenih Al2O3 vlakana. Cilj ovog rada bio je ispitivanje mehaničkih svojstava hibridnog kompozita, koji se sastoji od polimerne matrice (kopolimer etilena i vinil-acetata (EVA)), polietilenskih vlakana ultra-visoke molarne mase (UHMWPE) i Al2O3 vlakana dobijenih elektropredenjem. Al2O3 vlakna su dodavana u količini od 1 mas. % što je pokazalo poboljšanje mehaničkih svojstava matrice i hibridnog kompozita.
Alumina (Al2O3) nano fibers are prepared from an aqueous solution of aluminum hydroxy chloride/poly (vinyl alcohol) (PVA)/water using the electrospinning technique. The weight ratio of aluminum hydroxy chloride/PVA was 5: 1. After calcification of fibers at 1100 ° C, continuous aluminum oxide fibers were obtained from 200 to 800 nm. The fiber morphology is characterized by a scanning electron microscope (SEM). Image analysis software (Image Pro Plus) was used to measure the diameter of the obtained aluminum oxide (Al2O3) fibers. The aim of this paper is to examine the mechanical properties of the hybrid composite, consisting of a polymer matrix (ethylene and vinyl acetate copolymer (EVA)), ultrahigh molecular weight polyethylene fibers (UHMWPE) and Al2O3 fibers obtained by electrospinning. Al2O3 fibers were added in an amount of 1 wt. % as shown by the improvement of the mechanical properties of the matrix and the hybrid composite.
Keywords:
elektropredenje / Al2O3 vlakna / mehanička svojstva / EVA matrica / UHMWPE / Electrospinning / Al2O3 fibers / mechanical properties / EVA matrix / UHMWPESource:
Tehnika, 2018, 73, 6, 757-761Publisher:
- Savez inženjera i tehničara Srbije
Funding / projects:
- Predefined functional properties polymer composite materials processes and equipment development (RS-34011)
- Synthesis, processing and applications of nanostructured multifunctional materials with defined properties (RS-45019)
Collections
Institution/Community
Tehnološko-metalurški fakultetTY - JOUR AU - Zec, Jelena AU - Tomić, Nataša AU - Vuksanović, Marija M. AU - Veljović, Đorđe AU - Stojanović, Dušica AU - Jančić-Heinemann, Radmila PY - 2018 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3808 AB - Aluminijum oksidna (Al2O3) nanovlakna pripremljena su iz vodenog rastvora aluminijum hlorohidrata/poli(vinil alkohola) (PVA) korišćenjem tehnike elektropredenja. Maseni odnos aluminijum hlorohidrata/PVA bio je 5:1. Nakon kalcinacije vlakana na 1100 °C, dobijena su kratka aluminijum oksidna vlakna prečnika od 200 do 800 nm. Morfologija vlakana je karakterisana pomoću skenirajućeg elektronskog mikroskopa sa emisijom polja (FE-SEM). Softver za analizu slike Image ProPlus korišćen je za merenje prečnika dobijenih Al2O3 vlakana. Cilj ovog rada bio je ispitivanje mehaničkih svojstava hibridnog kompozita, koji se sastoji od polimerne matrice (kopolimer etilena i vinil-acetata (EVA)), polietilenskih vlakana ultra-visoke molarne mase (UHMWPE) i Al2O3 vlakana dobijenih elektropredenjem. Al2O3 vlakna su dodavana u količini od 1 mas. % što je pokazalo poboljšanje mehaničkih svojstava matrice i hibridnog kompozita. AB - Alumina (Al2O3) nano fibers are prepared from an aqueous solution of aluminum hydroxy chloride/poly (vinyl alcohol) (PVA)/water using the electrospinning technique. The weight ratio of aluminum hydroxy chloride/PVA was 5: 1. After calcification of fibers at 1100 ° C, continuous aluminum oxide fibers were obtained from 200 to 800 nm. The fiber morphology is characterized by a scanning electron microscope (SEM). Image analysis software (Image Pro Plus) was used to measure the diameter of the obtained aluminum oxide (Al2O3) fibers. The aim of this paper is to examine the mechanical properties of the hybrid composite, consisting of a polymer matrix (ethylene and vinyl acetate copolymer (EVA)), ultrahigh molecular weight polyethylene fibers (UHMWPE) and Al2O3 fibers obtained by electrospinning. Al2O3 fibers were added in an amount of 1 wt. % as shown by the improvement of the mechanical properties of the matrix and the hybrid composite. PB - Savez inženjera i tehničara Srbije T2 - Tehnika T1 - Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem T1 - Mechanical properties of UHMWPE/EVA hybrid composite reinforced with fibers obtained by electrospinning EP - 761 IS - 6 SP - 757 VL - 73 DO - 10.5937/tehnika1806757Z ER -
@article{ author = "Zec, Jelena and Tomić, Nataša and Vuksanović, Marija M. and Veljović, Đorđe and Stojanović, Dušica and Jančić-Heinemann, Radmila", year = "2018", abstract = "Aluminijum oksidna (Al2O3) nanovlakna pripremljena su iz vodenog rastvora aluminijum hlorohidrata/poli(vinil alkohola) (PVA) korišćenjem tehnike elektropredenja. Maseni odnos aluminijum hlorohidrata/PVA bio je 5:1. Nakon kalcinacije vlakana na 1100 °C, dobijena su kratka aluminijum oksidna vlakna prečnika od 200 do 800 nm. Morfologija vlakana je karakterisana pomoću skenirajućeg elektronskog mikroskopa sa emisijom polja (FE-SEM). Softver za analizu slike Image ProPlus korišćen je za merenje prečnika dobijenih Al2O3 vlakana. Cilj ovog rada bio je ispitivanje mehaničkih svojstava hibridnog kompozita, koji se sastoji od polimerne matrice (kopolimer etilena i vinil-acetata (EVA)), polietilenskih vlakana ultra-visoke molarne mase (UHMWPE) i Al2O3 vlakana dobijenih elektropredenjem. Al2O3 vlakna su dodavana u količini od 1 mas. % što je pokazalo poboljšanje mehaničkih svojstava matrice i hibridnog kompozita., Alumina (Al2O3) nano fibers are prepared from an aqueous solution of aluminum hydroxy chloride/poly (vinyl alcohol) (PVA)/water using the electrospinning technique. The weight ratio of aluminum hydroxy chloride/PVA was 5: 1. After calcification of fibers at 1100 ° C, continuous aluminum oxide fibers were obtained from 200 to 800 nm. The fiber morphology is characterized by a scanning electron microscope (SEM). Image analysis software (Image Pro Plus) was used to measure the diameter of the obtained aluminum oxide (Al2O3) fibers. The aim of this paper is to examine the mechanical properties of the hybrid composite, consisting of a polymer matrix (ethylene and vinyl acetate copolymer (EVA)), ultrahigh molecular weight polyethylene fibers (UHMWPE) and Al2O3 fibers obtained by electrospinning. Al2O3 fibers were added in an amount of 1 wt. % as shown by the improvement of the mechanical properties of the matrix and the hybrid composite.", publisher = "Savez inženjera i tehničara Srbije", journal = "Tehnika", title = "Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem, Mechanical properties of UHMWPE/EVA hybrid composite reinforced with fibers obtained by electrospinning", pages = "761-757", number = "6", volume = "73", doi = "10.5937/tehnika1806757Z" }
Zec, J., Tomić, N., Vuksanović, M. M., Veljović, Đ., Stojanović, D.,& Jančić-Heinemann, R.. (2018). Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem. in Tehnika Savez inženjera i tehničara Srbije., 73(6), 757-761. https://doi.org/10.5937/tehnika1806757Z
Zec J, Tomić N, Vuksanović MM, Veljović Đ, Stojanović D, Jančić-Heinemann R. Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem. in Tehnika. 2018;73(6):757-761. doi:10.5937/tehnika1806757Z .
Zec, Jelena, Tomić, Nataša, Vuksanović, Marija M., Veljović, Đorđe, Stojanović, Dušica, Jančić-Heinemann, Radmila, "Mehanička svojstva hibridnog kompozita UHMWPE/EVA ojačanog vlaknima dobijenim elektropredenjem" in Tehnika, 73, no. 6 (2018):757-761, https://doi.org/10.5937/tehnika1806757Z . .