TechnoRep - Faculty of Technology and Metallurgy Repository
University of Belgrade - Faculty of Technology and Metallurgy
    • English
    • Српски
    • Српски (Serbia)
  • English 
    • English
    • Serbian (Cyrillic)
    • Serbian (Latin)
  • Login
View Item 
  •   TechnoRep
  • Tehnološko-metalurški fakultet
  • Radovi istraživača / Researchers’ publications (TMF)
  • View Item
  •   TechnoRep
  • Tehnološko-metalurški fakultet
  • Radovi istraživača / Researchers’ publications (TMF)
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.

Physical Properties of Sintered Alumina Doped with Different Oxides

Thumbnail
2018
3906.pdf (1.466Mb)
Authors
Filipović, Suzana
Obradović, Nina
Marković, Smilja
Đorđević, Antonije
Balać, Igor
Dapčević, Aleksandra
Rogan, Jelena
Pavlović, Vladimir B.
Article (Published version)
Metadata
Show full item record
Abstract
Corundum (alpha-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 degrees C and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm(3). Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respec...tively, for the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.

Keywords:
Mechanical activation / Densities / SEM / Sintering / Alumina
Source:
Science of Sintering, 2018, 50, 4, 409-419
Publisher:
  • Međunarodni Institut za nauku o sinterovanju, Beograd
Funding / projects:
  • Directed synthesis, structure and properties of multifunctional materials (RS-172057)
  • Zero- to Three-Dimensional Nanostructures for Application in Electronics and Renewable Energy Sources: Synthesis, Characterization and Processing (RS-45007)
  • Synthesis, processing and applications of nanostructured multifunctional materials with defined properties (RS-45019)

DOI: 10.2298/SOS1804409F

ISSN: 0350-820X

WoS: 000455876800003

Scopus: 2-s2.0-85062894934
[ Google Scholar ]
14
11
URI
http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3909
Collections
  • Radovi istraživača / Researchers’ publications (TMF)
Institution/Community
Tehnološko-metalurški fakultet
TY  - JOUR
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Marković, Smilja
AU  - Đorđević, Antonije
AU  - Balać, Igor
AU  - Dapčević, Aleksandra
AU  - Rogan, Jelena
AU  - Pavlović, Vladimir B.
PY  - 2018
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3909
AB  - Corundum (alpha-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 degrees C and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm(3). Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.
PB  - Međunarodni Institut za nauku o sinterovanju, Beograd
T2  - Science of Sintering
T1  - Physical Properties of Sintered Alumina Doped with Different Oxides
EP  - 419
IS  - 4
SP  - 409
VL  - 50
DO  - 10.2298/SOS1804409F
ER  - 
@article{
author = "Filipović, Suzana and Obradović, Nina and Marković, Smilja and Đorđević, Antonije and Balać, Igor and Dapčević, Aleksandra and Rogan, Jelena and Pavlović, Vladimir B.",
year = "2018",
abstract = "Corundum (alpha-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 degrees C and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm(3). Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Physical Properties of Sintered Alumina Doped with Different Oxides",
pages = "419-409",
number = "4",
volume = "50",
doi = "10.2298/SOS1804409F"
}
Filipović, S., Obradović, N., Marković, S., Đorđević, A., Balać, I., Dapčević, A., Rogan, J.,& Pavlović, V. B.. (2018). Physical Properties of Sintered Alumina Doped with Different Oxides. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 50(4), 409-419.
https://doi.org/10.2298/SOS1804409F
Filipović S, Obradović N, Marković S, Đorđević A, Balać I, Dapčević A, Rogan J, Pavlović VB. Physical Properties of Sintered Alumina Doped with Different Oxides. in Science of Sintering. 2018;50(4):409-419.
doi:10.2298/SOS1804409F .
Filipović, Suzana, Obradović, Nina, Marković, Smilja, Đorđević, Antonije, Balać, Igor, Dapčević, Aleksandra, Rogan, Jelena, Pavlović, Vladimir B., "Physical Properties of Sintered Alumina Doped with Different Oxides" in Science of Sintering, 50, no. 4 (2018):409-419,
https://doi.org/10.2298/SOS1804409F . .

DSpace software copyright © 2002-2015  DuraSpace
About TechnoRep | Send Feedback

OpenAIRERCUB
 

 

All of DSpaceInstitutions/communitiesAuthorsTitlesSubjectsThis institutionAuthorsTitlesSubjects

Statistics

View Usage Statistics

DSpace software copyright © 2002-2015  DuraSpace
About TechnoRep | Send Feedback

OpenAIRERCUB