Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correlation (DIC) technique. For this purpose, specimens were taken from butt welded plates, made of P460NL1 micro-alloyed steel. Fatigue pre-crack of 3PB specimens was introduced in the weld metal. Specimens were then statically loaded and analyzed using digital image correlation software ARAMIS to assess strain fields and crack propagation paths. Bifurcation of cracks was noticed as the main characteristics of crack prop-agation in the analyzed case.
TY - JOUR
AU - Aranđelović, M.
AU - Sedmak, S. A.
AU - Milović, Ljubica
AU - Maksimović, Ana
AU - Bozic, Z.
PY - 2020
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/4754
AB - Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correlation (DIC) technique. For this purpose, specimens were taken from butt welded plates, made of P460NL1 micro-alloyed steel. Fatigue pre-crack of 3PB specimens was introduced in the weld metal. Specimens were then statically loaded and analyzed using digital image correlation software ARAMIS to assess strain fields and crack propagation paths. Bifurcation of cracks was noticed as the main characteristics of crack prop-agation in the analyzed case.
T2 - 1st Virtual European Conference on Fracture - Vecf1
T1 - Crack propagation in 3PB specimen made from welded joint
EP - 445
SP - 440
VL - 28
DO - 10.1016/j.prostr.2020.10.051
ER -
@article{
author = "Aranđelović, M. and Sedmak, S. A. and Milović, Ljubica and Maksimović, Ana and Bozic, Z.",
year = "2020",
abstract = "Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correlation (DIC) technique. For this purpose, specimens were taken from butt welded plates, made of P460NL1 micro-alloyed steel. Fatigue pre-crack of 3PB specimens was introduced in the weld metal. Specimens were then statically loaded and analyzed using digital image correlation software ARAMIS to assess strain fields and crack propagation paths. Bifurcation of cracks was noticed as the main characteristics of crack prop-agation in the analyzed case.",
journal = "1st Virtual European Conference on Fracture - Vecf1",
title = "Crack propagation in 3PB specimen made from welded joint",
pages = "445-440",
volume = "28",
doi = "10.1016/j.prostr.2020.10.051"
}
Aranđelović, M., Sedmak, S. A., Milović, L., Maksimović, A.,& Bozic, Z.. (2020). Crack propagation in 3PB specimen made from welded joint. in 1st Virtual European Conference on Fracture - Vecf1, 28, 440-445.
https://doi.org/10.1016/j.prostr.2020.10.051
Aranđelović M, Sedmak SA, Milović L, Maksimović A, Bozic Z. Crack propagation in 3PB specimen made from welded joint. in 1st Virtual European Conference on Fracture - Vecf1. 2020;28:440-445.
doi:10.1016/j.prostr.2020.10.051 .
Aranđelović, M., Sedmak, S. A., Milović, Ljubica, Maksimović, Ana, Bozic, Z., "Crack propagation in 3PB specimen made from welded joint" in 1st Virtual European Conference on Fracture - Vecf1, 28 (2020):440-445,
https://doi.org/10.1016/j.prostr.2020.10.051 . .