PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.
TY - JOUR
AU - Branković, Zorica
AU - Branković, Goran
AU - Varela, JA
PY - 2003
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5398
AB - PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.
PB - Kluwer Academic Publ, Dordrecht
T2 - Journal of Materials Science-Materials in Electronics
T1 - PZT ceramics obtained from mechanochemically synthesized powders
EP - 41
IS - 1
SP - 37
VL - 14
DO - 10.1023/A:1021527615661
ER -
@article{
author = "Branković, Zorica and Branković, Goran and Varela, JA",
year = "2003",
abstract = "PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.",
publisher = "Kluwer Academic Publ, Dordrecht",
journal = "Journal of Materials Science-Materials in Electronics",
title = "PZT ceramics obtained from mechanochemically synthesized powders",
pages = "41-37",
number = "1",
volume = "14",
doi = "10.1023/A:1021527615661"
}
Branković, Z., Branković, G.,& Varela, J.. (2003). PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics
Kluwer Academic Publ, Dordrecht., 14(1), 37-41.
https://doi.org/10.1023/A:1021527615661
Branković Z, Branković G, Varela J. PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics. 2003;14(1):37-41.
doi:10.1023/A:1021527615661 .
Branković, Zorica, Branković, Goran, Varela, JA, "PZT ceramics obtained from mechanochemically synthesized powders" in Journal of Materials Science-Materials in Electronics, 14, no. 1 (2003):37-41,
https://doi.org/10.1023/A:1021527615661 . .