Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction

Elezovic, N. R.; Babić, Biljana M.; Radmilovíć, Velimir R.; Vracar, Lj. M.; Krstajic, N. V.

doi:10.1016/j.apcatb.2013.04.012

Само за регистроване кориснике

2013

Аутори

Elezovic, N. R.
Babić, Biljana M.
Radmilovíć, Velimir R.
Vracar, Lj. M.
Krstajic, N. V.

Чланак у часопису (Објављена верзија)

Метаподаци

Приказ свих података о документу

Апстракт

Ruthenium doped titanium oxide support was synthesized. The support was characterized by BET (Brunauer, Emmett, Teller) and X-ray diffraction techniques (XRD). Determined specific surface area was 41 m(2) g(-1). XRD revealed presence mainly TiO2 anatase phase and some peaks belonging to rutile phase. No Ru compounds have been detected. Platinum based catalyst on this support was prepared by borohydride reduction method. The catalyst was characterized by scanning transmission electron microscopy (STEM, HAADF) and electron energy loss spectroscopy (EELS). Homogenous Pt particle distribution over the support, with average Pt nanoparticle diameter of 3 nm was found. This novel catalyst was tested for oxygen reduction in acid solution. It exhibited remarkable higher catalytic activity in comparison with Pt/C, as well as with Pt nanocatalysts at titanium oxide based supports, reported in literature. (C) 2013 Elsevier B.V. All rights reserved.

Кључне речи:

Titanium oxide based support / Pt/RuTiO2 catalyst / Oxygen reduction reaction / Acid solution

Извор:
Applied Catalysis. B: Environmental, 2013, 140, 206-212

Финансирање / пројекти:

Reinforcing of Nanotechnology and Functional Materials Centre (EU-245916)
Развој, карактеризација и примена наноструктуираних композитних катализатора и интерактивних носача у горивним спреговима и електролизи воде (RS-172054)
Office of Science, Office of Basic Energy Sciences, of the U.S. Department of Energy [DE-AC02-05CH11231], Nanotechnology and Functional Materials Center, Serbian Academy of Sciences and Arts

DOI: 10.1016/j.apcatb.2013.04.012

ISSN: 0926-3373

WoS: 000321991300024

Scopus: 2-s2.0-84877047260

[ Google Scholar ]


	16
	13

TY  - JOUR
AU  - Elezovic, N. R.
AU  - Babić, Biljana M.
AU  - Radmilovíć, Velimir R.
AU  - Vracar, Lj. M.
AU  - Krstajic, N. V.
PY  - 2013
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5707
AB  - Ruthenium doped titanium oxide support was synthesized. The support was characterized by BET (Brunauer, Emmett, Teller) and X-ray diffraction techniques (XRD). Determined specific surface area was 41 m(2) g(-1). XRD revealed presence mainly TiO2 anatase phase and some peaks belonging to rutile phase. No Ru compounds have been detected. Platinum based catalyst on this support was prepared by borohydride reduction method. The catalyst was characterized by scanning transmission electron microscopy (STEM, HAADF) and electron energy loss spectroscopy (EELS). Homogenous Pt particle distribution over the support, with average Pt nanoparticle diameter of 3 nm was found. This novel catalyst was tested for oxygen reduction in acid solution. It exhibited remarkable higher catalytic activity in comparison with Pt/C, as well as with Pt nanocatalysts at titanium oxide based supports, reported in literature. (C) 2013 Elsevier B.V. All rights reserved.
T2  - Applied Catalysis. B: Environmental
T1  - Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction
EP  - 212
SP  - 206
VL  - 140
DO  - 10.1016/j.apcatb.2013.04.012
ER  -

@article{
author = "Elezovic, N. R. and Babić, Biljana M. and Radmilovíć, Velimir R. and Vracar, Lj. M. and Krstajic, N. V.",
year = "2013",
abstract = "Ruthenium doped titanium oxide support was synthesized. The support was characterized by BET (Brunauer, Emmett, Teller) and X-ray diffraction techniques (XRD). Determined specific surface area was 41 m(2) g(-1). XRD revealed presence mainly TiO2 anatase phase and some peaks belonging to rutile phase. No Ru compounds have been detected. Platinum based catalyst on this support was prepared by borohydride reduction method. The catalyst was characterized by scanning transmission electron microscopy (STEM, HAADF) and electron energy loss spectroscopy (EELS). Homogenous Pt particle distribution over the support, with average Pt nanoparticle diameter of 3 nm was found. This novel catalyst was tested for oxygen reduction in acid solution. It exhibited remarkable higher catalytic activity in comparison with Pt/C, as well as with Pt nanocatalysts at titanium oxide based supports, reported in literature. (C) 2013 Elsevier B.V. All rights reserved.",
journal = "Applied Catalysis. B: Environmental",
title = "Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction",
pages = "212-206",
volume = "140",
doi = "10.1016/j.apcatb.2013.04.012"
}

Elezovic, N. R., Babić, B. M., Radmilovíć, V. R., Vracar, Lj. M.,& Krstajic, N. V.. (2013). Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction. in Applied Catalysis. B: Environmental, 140, 206-212.
https://doi.org/10.1016/j.apcatb.2013.04.012

Elezovic NR, Babić BM, Radmilovíć VR, Vracar LM, Krstajic NV. Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction. in Applied Catalysis. B: Environmental. 2013;140:206-212.
doi:10.1016/j.apcatb.2013.04.012 .

Elezovic, N. R., Babić, Biljana M., Radmilovíć, Velimir R., Vracar, Lj. M., Krstajic, N. V., "Novel Pt catalyst on ruthenium doped TiO2 support for oxygen reduction reaction" in Applied Catalysis. B: Environmental, 140 (2013):206-212,
https://doi.org/10.1016/j.apcatb.2013.04.012 . .