@article{
author = "Ivanović, Jasna and Knauer, Sandra and Fanovich, Alejandra and Milovanović, Stoja and Stamenić, Marko and Jaeger, Philip and Žižović, Irena and Eggers, Rudolf",
year = "2016",
abstract = "The potential of supercritical carbon dioxide (scCO(2)) processing of polycaprolactone (Pa) and polycaprolactone-hydroxyapatite (PCL-HA) composites for obtaining functional porous scaffolds at moderate temperatures (35-40 degrees C) was analyzed and quantified. The effect of scCO(2) sorption kinetics on the swelling, foam morphology and thermal behavior of the PCL and PCL-HA composites was studied. Sorption isotherms were determined using magnetic suspension balance at 10-30 MPa and 35-40 degrees C. Influence of the pressure, HA amount (10-20%) and procedure for HA powder preparation on the sorption kinetics was discussed. Supercritical solvent impregnation (SSI) of PCL and PCL-HA with thymol was investigated as environmentally friendly way to produce functional scaffolds with controlled microstructure. Moderately high pressures (13-17 MPa) and 10% of HA were proven to be favorable for creation of the PCL scaffolds with satisfying foam microstructure (mean pore size similar to 200-300 mu m), filler distribution and thymol impregnation yields (12-18%). This was due to the satisfactory high scCO(2) solubility (0.25-0.30 g/g) and mass transfer rate (similar to 10(-10) m(2)/s) in the polymer phase as well as its great plasticizing effect (-Delta T-m = 26.4-27.4 degrees C). Higher saturation of the polymer phase with scCO(2) (0.30-0.55 g/g), filler amount (20%) and thymol solubility in scCO(2) ( gt 5.5 g/kg) at pressures above 20 MPa resulted in decreased mass transfer rate and SSI efficiency.",
publisher = "Elsevier, Amsterdam",
journal = "Journal of Supercritical Fluids",
title = "Supercritical CO2 sorption kinetics and thymol impregnation of PCL and PCL-HA",
pages = "498-486",
volume = "107",
doi = "10.1016/j.supflu.2015.07.001"
}