The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings
Само за регистроване кориснике
2013
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Zn - Mn alloy electrodeposition on steel electrode, in electrolytes containing chloride or sulfate anions, was investigated by chronopotentiometry. Galvanostatically obtained electrodeposits were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), and atomic absorption spectrophotometry (AAS). It was found that Zn2+ and Mn2+ ion reduction occurred at higher overpotentials in sulfate bath, leading to a higher Mn content in the deposit and smaller crystallites as compared to the chloride electrolyte. AFM images of deposits revealed that with the increase in deposition current density, bigger agglomerates formed in both electrolytes, leading to higher roughness and heterogeneity of the samples. In relation to this observation, the Zn - Mn coatings were deposited at current densities of up to 80 mA cm(-2) because at higher current densities the samples from sulfate electrolyte were non adherent and dendritic. Depending on the deposition current density, the XRD pattern...s of the Zn - Mn deposits produced from chloride electrolyte indicated that the coatings were formed of either eta- or epsilon-Zn-Mn phase, while the coatings obtained from sulfate bath consisted of epsilon-Zn - Mn phase. The linear polarization method showed that Zn - Mn alloys deposited from sulfate electrolyte exhibited higher corrosion resistance in NaCl corrosive media.
Кључне речи:
Electrochemical deposition / Zn - Mn alloy / X-ray diffraction (XRD) / Atomic force microscopy (AFM) / CorrosionИзвор:
Surface & Coatings Technology, 2013, 228, 221-228Издавач:
- Elsevier Science Sa, Lausanne
Финансирање / пројекти:
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45019)
DOI: 10.1016/j.surfcoat.2013.04.032
ISSN: 0257-8972
WoS: 000321797100026
Scopus: 2-s2.0-84879463587
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Bucko, M. AU - Rogan, Jelena AU - Stevanović, Sanja AU - Stanković, S. AU - Bajat, Jelena PY - 2013 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2414 AB - Zn - Mn alloy electrodeposition on steel electrode, in electrolytes containing chloride or sulfate anions, was investigated by chronopotentiometry. Galvanostatically obtained electrodeposits were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), and atomic absorption spectrophotometry (AAS). It was found that Zn2+ and Mn2+ ion reduction occurred at higher overpotentials in sulfate bath, leading to a higher Mn content in the deposit and smaller crystallites as compared to the chloride electrolyte. AFM images of deposits revealed that with the increase in deposition current density, bigger agglomerates formed in both electrolytes, leading to higher roughness and heterogeneity of the samples. In relation to this observation, the Zn - Mn coatings were deposited at current densities of up to 80 mA cm(-2) because at higher current densities the samples from sulfate electrolyte were non adherent and dendritic. Depending on the deposition current density, the XRD patterns of the Zn - Mn deposits produced from chloride electrolyte indicated that the coatings were formed of either eta- or epsilon-Zn-Mn phase, while the coatings obtained from sulfate bath consisted of epsilon-Zn - Mn phase. The linear polarization method showed that Zn - Mn alloys deposited from sulfate electrolyte exhibited higher corrosion resistance in NaCl corrosive media. PB - Elsevier Science Sa, Lausanne T2 - Surface & Coatings Technology T1 - The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings EP - 228 SP - 221 VL - 228 DO - 10.1016/j.surfcoat.2013.04.032 ER -
@article{ author = "Bucko, M. and Rogan, Jelena and Stevanović, Sanja and Stanković, S. and Bajat, Jelena", year = "2013", abstract = "Zn - Mn alloy electrodeposition on steel electrode, in electrolytes containing chloride or sulfate anions, was investigated by chronopotentiometry. Galvanostatically obtained electrodeposits were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), and atomic absorption spectrophotometry (AAS). It was found that Zn2+ and Mn2+ ion reduction occurred at higher overpotentials in sulfate bath, leading to a higher Mn content in the deposit and smaller crystallites as compared to the chloride electrolyte. AFM images of deposits revealed that with the increase in deposition current density, bigger agglomerates formed in both electrolytes, leading to higher roughness and heterogeneity of the samples. In relation to this observation, the Zn - Mn coatings were deposited at current densities of up to 80 mA cm(-2) because at higher current densities the samples from sulfate electrolyte were non adherent and dendritic. Depending on the deposition current density, the XRD patterns of the Zn - Mn deposits produced from chloride electrolyte indicated that the coatings were formed of either eta- or epsilon-Zn-Mn phase, while the coatings obtained from sulfate bath consisted of epsilon-Zn - Mn phase. The linear polarization method showed that Zn - Mn alloys deposited from sulfate electrolyte exhibited higher corrosion resistance in NaCl corrosive media.", publisher = "Elsevier Science Sa, Lausanne", journal = "Surface & Coatings Technology", title = "The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings", pages = "228-221", volume = "228", doi = "10.1016/j.surfcoat.2013.04.032" }
Bucko, M., Rogan, J., Stevanović, S., Stanković, S.,& Bajat, J.. (2013). The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings. in Surface & Coatings Technology Elsevier Science Sa, Lausanne., 228, 221-228. https://doi.org/10.1016/j.surfcoat.2013.04.032
Bucko M, Rogan J, Stevanović S, Stanković S, Bajat J. The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings. in Surface & Coatings Technology. 2013;228:221-228. doi:10.1016/j.surfcoat.2013.04.032 .
Bucko, M., Rogan, Jelena, Stevanović, Sanja, Stanković, S., Bajat, Jelena, "The influence of anion type in electrolyte on the properties of electrodeposited Zn-Mn alloy coatings" in Surface & Coatings Technology, 228 (2013):221-228, https://doi.org/10.1016/j.surfcoat.2013.04.032 . .