Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy
Autori
Volkov-Husović, TatjanaIvanic, Ivana
Kozuh, Stjepan
Stevanovic, Sanja
Vlahovic, Milica
Martinovic, Sanja
Stopic, Srecko
Gojic, Mirko
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Microstructural and cavitation erosion testing was carried out on Cu-12.8Al-4.1Ni (wt. %) shape memory alloy (SMA) samples produced by continuous casting followed by heat treatment consisting of solution annealing at 885 degrees C for 60 min and, later, water quenching. Cavitation resistance testing was applied using a standard ultrasonic vibratory cavitation set up with stationary specimen. Surface changes during the cavitation were monitored by metallographic analysis using an optical microscope (OM), atomic force microscope (AFM), and scanning electron microscope (SEM) as well as by weight measurements. The results revealed a martensite microstructure after both casting and quenching. Microhardness value was higher after water quenching than in the as-cast state. After 420 min of cavitation exposure, a negligible mass loss was noticed for both samples. Based on the obtained results, both samples showed excellent cavitation resistance. Mass loss and morphological analysis of the form...ed pits indicated better cavitation resistance for the as-cast state (L).
Ključne reči:
cavitation erosion / optical microscopy / electron microscopy / atomic force microscopyIzvor:
Metals, 2021, 11, 7Finansiranje / projekti:
- Ministarstvo nauke, tehnološkog razvoja i inovacija Republike Srbije, institucionalno finansiranje - 200026 (Univerzitet u Beogradu, Institut za hemiju, tehnologiju i metalurgiju - IHTM) (RS-MESTD-inst-2020-200026)
- Ministarstvo nauke, tehnološkog razvoja i inovacija Republike Srbije, institucionalno finansiranje - 200135 (Univerzitet u Beogradu, Tehnološko-metalurški fakultet) (RS-MESTD-inst-2020-200135)
DOI: 10.3390/met11070997
ISSN: 2075-4701
WoS: 000676247800001
Scopus: 2-s2.0-85108239118
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Volkov-Husović, Tatjana AU - Ivanic, Ivana AU - Kozuh, Stjepan AU - Stevanovic, Sanja AU - Vlahovic, Milica AU - Martinovic, Sanja AU - Stopic, Srecko AU - Gojic, Mirko PY - 2021 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/4862 AB - Microstructural and cavitation erosion testing was carried out on Cu-12.8Al-4.1Ni (wt. %) shape memory alloy (SMA) samples produced by continuous casting followed by heat treatment consisting of solution annealing at 885 degrees C for 60 min and, later, water quenching. Cavitation resistance testing was applied using a standard ultrasonic vibratory cavitation set up with stationary specimen. Surface changes during the cavitation were monitored by metallographic analysis using an optical microscope (OM), atomic force microscope (AFM), and scanning electron microscope (SEM) as well as by weight measurements. The results revealed a martensite microstructure after both casting and quenching. Microhardness value was higher after water quenching than in the as-cast state. After 420 min of cavitation exposure, a negligible mass loss was noticed for both samples. Based on the obtained results, both samples showed excellent cavitation resistance. Mass loss and morphological analysis of the formed pits indicated better cavitation resistance for the as-cast state (L). T2 - Metals T1 - Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy IS - 7 VL - 11 DO - 10.3390/met11070997 ER -
@article{ author = "Volkov-Husović, Tatjana and Ivanic, Ivana and Kozuh, Stjepan and Stevanovic, Sanja and Vlahovic, Milica and Martinovic, Sanja and Stopic, Srecko and Gojic, Mirko", year = "2021", abstract = "Microstructural and cavitation erosion testing was carried out on Cu-12.8Al-4.1Ni (wt. %) shape memory alloy (SMA) samples produced by continuous casting followed by heat treatment consisting of solution annealing at 885 degrees C for 60 min and, later, water quenching. Cavitation resistance testing was applied using a standard ultrasonic vibratory cavitation set up with stationary specimen. Surface changes during the cavitation were monitored by metallographic analysis using an optical microscope (OM), atomic force microscope (AFM), and scanning electron microscope (SEM) as well as by weight measurements. The results revealed a martensite microstructure after both casting and quenching. Microhardness value was higher after water quenching than in the as-cast state. After 420 min of cavitation exposure, a negligible mass loss was noticed for both samples. Based on the obtained results, both samples showed excellent cavitation resistance. Mass loss and morphological analysis of the formed pits indicated better cavitation resistance for the as-cast state (L).", journal = "Metals", title = "Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy", number = "7", volume = "11", doi = "10.3390/met11070997" }
Volkov-Husović, T., Ivanic, I., Kozuh, S., Stevanovic, S., Vlahovic, M., Martinovic, S., Stopic, S.,& Gojic, M.. (2021). Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy. in Metals, 11(7). https://doi.org/10.3390/met11070997
Volkov-Husović T, Ivanic I, Kozuh S, Stevanovic S, Vlahovic M, Martinovic S, Stopic S, Gojic M. Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy. in Metals. 2021;11(7). doi:10.3390/met11070997 .
Volkov-Husović, Tatjana, Ivanic, Ivana, Kozuh, Stjepan, Stevanovic, Sanja, Vlahovic, Milica, Martinovic, Sanja, Stopic, Srecko, Gojic, Mirko, "Microstructural and Cavitation Erosion Behavior of the CuAlNi Shape Memory Alloy" in Metals, 11, no. 7 (2021), https://doi.org/10.3390/met11070997 . .