Претраживање
Приказ резултата 1-10 од 10
Influence of heat transfer conditions on determination of thermal shock resistance of refractories / Uticaj prenosa toplote na određivanje termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The goal of this thesis was to determine the thermal shock resistance of alumina based refractories in the case of a heat transfer conditions different from the standard conditions given by quenching test JUS. B. D.8 319. ...
The growth of germanijum single crystal in the universal multizone crystallization furnace by application of the electronic Bridgman-Stocbarger method / Rast monokristala germanijuma u univerzalnom multizonskom kristalizatoru primenom elektronske Bridgman-Stocbarger metode
(Savez inženjera metalurgije Srbije, Beograd, 2002)
This paper examines the possibility of the application of multizone furnace, i.e. universal multizone crystallizator furnace in obtaining germanijum (Ga added) single crystal using electronic Bridgman-Stocbarger method. ...
Thermomechanical processing of micro alloyed steels in Sartid A.D.: Part III - comparison of of Tnr temperatures determined on laboratory and industrial scale / Termomehanička prerada mikrolegiranih čelika koncerna Sartid: III deo - poređenje Tnr temperatura određenih u laboratorijskim i industrijskim uslovima
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The aim of this work was to compare the Tnr temperatures of microalloyed steels estimated on laboratory (Tnr**l) and industrial scale (Tnr**l). Laboratory and industrial scale are related to testing on high temperature ...
Rotating disk alumina precursor fiber formation process stability determination using image analysis
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Precursor fibers are made from the aluminium-hydroxide chloride based sols. The process stability can be influenced both by the fiber formation conditions and the rheology of the sol. The distance from the disk canter is ...
Dependence of the solid-liquid interface structure on the solidification process parameters / Zavisnost strukture granice faza tečno-čvrsto od parametara procesa očvršćavanja
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Influence of the solidification rate, temperature gradient and initial concentration of the solute on the interface shape was investigated during solidification from the melt. The dependence of the microstructure on the ...
The influence of the solidification rate on the interface shape and distribution of solute
(Savez inženjera metalurgije Srbije, Beograd, 2002)
In this paper investigation of the influence of the solidification conditions on the interface shape and distribution of solute during the solidification of AI-Cu alloy by vertical Bridgman method were investigated. The ...
The effects of thermomechanical treatment on the SCC resistance of highly alloyed Al-Mg sheet / Uticaj termomehaničke obrade na otpornost prema naponskoj koroziji visoko legiranih Al-Mg limova
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The effects of cold work and different heat treatments on the stress corrosion cracking (SCC) behavior of Al-Mg6.8% alloy were studied using slow strain rate testing (SSRT). The results have indicated high SCC susceptibility ...
Monitoring the damage level during thermal stability testing of refractory sample using soninic measurement
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 28 % AI2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied as experimental method for thermal stability testing. Dynamic Young modulus of ...
Shot-peening induced twinning in ship-building steel / Dvojnikovanje u brodskom limu kao posledica tretiranja u mlazu sačme
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The aim of this work to simulate a shot-peening process and reveal the final microstructure. The latter consisted of rafinated ferritic grains, with occurrence of twins in some grains. Since the twinning occurs when a very ...
Investigation of dynamic young modulus during thermal stability testing of the refractory material / Određivanje dinamičkog jungovog modula elastičnosti tokom ispitivanja termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 42 % Al2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied. Photographs of the samples before cycling, and after some number of cycles were ...