Influence of heat transfer conditions on determination of thermal shock resistance of refractories / Uticaj prenosa toplote na određivanje termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The goal of this thesis was to determine the thermal shock resistance of alumina based refractories in the case of a heat transfer conditions different from the standard conditions given by quenching test JUS. B. D.8 319. ...
Monitoring the damage level during thermal stability testing of refractory sample using soninic measurement
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 28 % AI2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied as experimental method for thermal stability testing. Dynamic Young modulus of ...
Investigation of dynamic young modulus during thermal stability testing of the refractory material / Određivanje dinamičkog jungovog modula elastičnosti tokom ispitivanja termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 42 % Al2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied. Photographs of the samples before cycling, and after some number of cycles were ...
An improved method for thermal stability behavior characterization of silicon carbide/cordierite composite material
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 50:50. Samples were exposed to the water quench test from 950°C, ...