Thermal stability testing of refractory specimen
(Amer Soc Testing Materials, W Conshohocken, 2006)
The most important properties usually measured for refractories are working temperature and thermal stability. Thermal stability of the alumina based samples was measured using standard laboratory procedure, water quench ...
Rotating disk alumina precursor fiber formation process stability determination using image analysis
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Precursor fibers are made from the aluminium-hydroxide chloride based sols. The process stability can be influenced both by the fiber formation conditions and the rheology of the sol. The distance from the disk canter is ...
Influence of formation conditions and precursor viscosity on mean fiber diameter formed using the relating disk method
(Elsevier, Amsterdam, 2000)
Alumina ceramic fibers were produced from aluminum-hydroxidechloride based sol. Polyvinyl alcohol and surface active material were applied to adjust the rheological characteristics of the: sol. The rotating disk formation ...
The influence of the deposition parameters on the porosity of thin alumina films on steel / Uticaj parametara elektroforetskog taloženja praha aluminijum-oksida iz vodenih suspenzija na poroznost dobijenih tankih filmova na čeliku
(Serbian Chemical Society, Belgrade, 2004)
The influence of the deposition parameters on the porosity of thin alumina films electrophoretically deposited on steel from aqueous suspensions was investigated. The effects of the applied voltage, deposition time, ...
An improved method for thermal stability behavior characterization of silicon carbide/cordierite composite material
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 50:50. Samples were exposed to the water quench test from 950°C, ...
Determination of thermal shock resistance of silicon carbide/cordierite composite material using nondestructive test methods
(Elsevier Sci Ltd, Oxford, 2008)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 30:70 and 50:50. Behavior of composite ceramics after thermal ...
Microstructural dependence of fracture toughness in high-strength 7000 forging alloys
(Pergamon-Elsevier Science Ltd, Oxford, 2008)
The effects of microstructural parameters associated with the coarse intermetallic phases particles and precipitates on the fracture toughness of the overaged 7000 alloy forgings are investigated. Detailed microstructural ...