Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Electrospun Alumina Fibers Doped With Ferric and Magnesium Oxides
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
It is well known that alumina possesses good mechanical and chemical properties. Nanofibers having alpha - alumina structure was used as reinforcement for metal, polymer and ceramic matrix composites. In this study, three ...
Comparison of Morphological Parameters of Ceramic Materials Surface Damage Exposed to Thermal Shock and Cavitation Erosion
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The surface defects on the samples, which are based on alumina, exposed to thermal shocks and cavitations erosion were analyzed using image analysis. For both types of experimental testing, the samples are made of the same ...
Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M ...
Investigation of Possibility for Stabilization and Valorization of Electric Arc Furnace Dust and Glass From Electronic Waste
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
This paper presents investigation of possibility for electric arc furnace dust (EAFD) and electronic waste (e-waste) valorization trough stabilization process, in order to achieve concurrent management of these two serious ...
Characterization of MgAl2O4 Sintered Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...
Novel Approach for Determination of Potentially Toxic Elements via ICP-OES in Aqueous Solutions of Building Materials with Industrial Byproduct Addition
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
New global tendencies for waste materials reusing in building materials are imposing the request for improved performances of chemical analysis methods and the improvements of matrices used. A new method for optical emission ...
Anisotropy Analysis of Low Cement Concrete by Ultrasonic Measurements and Image Analysis
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The analized material was high alumina low cement castable sintered at three different temperatures. Influence of initial material anisotropy on the thermal shock resistance as well as changes of anisotropy level during ...
Alumina Particles Doped With Ferric as Efficient Adsorbent for Removal of Reactive Orange 16 from Aqueous Solutions
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
Ferric oxide doped alumina particles were prepared via the sol-gel method and their performance as Reactive Orange 16 adsorbent was evaluated. The concentrations of the Reactive Orange 16 were monitored using a UV-Vis ...
The effect of K2O on the crystallization of niobium germanate glasses
(International Institute for the Science of Sintering, Beograd, 2011)
The effect of K2O content on the crystallization of niobium germanate glasses with 22.7- 24.27 wt% of GeO2 and 54.59-57.48 wt% of Nb2O5 was examined. The glasses crystallize by primary crystallization and the formed ...