The effect of annealing temperatures on magnetic and electric properties of electrodeposited Ni85,3Fe10,6W1,4Cu2,2 alloy
(Natl Inst Optoelectronics, Bucharest-Magurele, 2014)
Ni-85,Ni-8 Fe-10,Fe-6 W-1,W-4 Cu-2,Cu-2 alloy powder consisting of an amorphous matrix and nanocrystals of an FCC solid solution of Fe, W and Cu in nickel was produced by electrodeposition. Heating the pressed powder sample ...
Corrosion Stability of Corrosion Products on an Archaeological Iron Artefact
(Alexandru Ioan Cuza University Publiching House Iasi-Romania, 2012)
A spearhead of archaeological and cultural significance has been found and analysed in
Serbia. In the corrosion products of the artefact, the dominant phases were goethite (α-
FeO(OH)) and magnetite (Fe3O4) whose presence ...
Solubility in the ternary system CaSO4 + Na2SO4 + H2O at 298.15 K
(Maik Nauka/Interperiodica/Springer, New York, 2011)
The solubility in the ternary system, aqueous mixture of CaSO4 and Na2SO4, at T = 298.15 K comprises five different salts: calcium sulfate dihydrate, mirabilite, thenardite, glauberite and labile salt. Using the Extended ...
Silver incorporation on viscose and cotton fibers after air, nitrogen and oxygen DBD plasma pretreatment
(Springer, Dordrecht, 2013)
Dielectric barrier discharge (DBD) pretreatments in air, nitrogen and oxygen plasma of viscose and cotton fabrics with subsequent immobilization of silver were studied. Surface activation of treated fibers was evaluated ...
Evaluation of alginate hydrogels under in vivo-like bioreactor conditions for cartilage tissue engineering
(Springer, Dordrecht, 2010)
Alginate hydrogels in forms of discs and packed beds of microbeads (similar to 800 mu m) were tested in a novel bioreactor at 10% strain using two regimes: at a loading rate of 337.5 mu m/s and at sequential increments of ...
The analysis of forming PVB-SiO2 nanocomposite fibers by the electrospinning process / Analiza formiranja PVB-SiO2 nanokompozitnih vlakana pomoću elektrospining procesa
(Military Technical Institute, Belgrade, 2011)
The poly (vinyl butyral)-silica (PVB-SiO2) nanofibers were obtained by the electrospinning process. The experiments were carried out with PVB solution in concentration of 10 wt.% where ethanol was used as the solvent. The ...
Influence of hemicelluloses and lignin content on structure and sorption properties of flax fibers (Linum usitatissimum L.)
(Springer, Dordrecht, 2018)
In this work, alkali and oxidative treatments were employed to obtain flax fibers with different content of hemicelluloses and lignin, in order to study the influence of chemical composition on structure and sorption ...
Study of interaction between nitrogen DBD plasma-treated viscose fibers and divalent ions Ca2+ and Cu2+
(Springer, Dordrecht, 2014)
Viscose fibers were treated with atmospheric pressure dielectric barrier discharge (DBD) plasma obtained in nitrogen in order to activate the fiber surface prior to sorption of the divalent ions Ca2+ and Cu2+. Methylene ...
Multipurpose nonwoven viscose/polypropylene fabrics: Effect of fabric characteristics on sorption and dielectric properties
(Wiley, Hoboken, 2018)
In this work, sorption and dielectric properties of viscose/polypropylene multipurpose nonwoven fabrics were examined. The analysis of sorption behavior showed that the changes of the water absorptive capacity, the height ...
Iron-Modified Sepiolite for Ni2+ Sorption from Aqueous Solution: An Equilibrium, Kinetic, and Thermodynamic Study
(Amer Chemical Soc, Washington, 2010)
Sepiolite was used for the synthesis of the sepiolite-iron oxide system to obtain a sorbent suitable for the removal of Ni2+ from aqueous solution. The modified material, Fe-sepiolite, was characterized by X-ray diffraction ...