Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5)
Само за регистроване кориснике
2014
Аутори
Pantić, Jelena R.Urbanovich, Vladimir
Poharc-Logar, Vesna
Jokić, Bojan M.
Stojmenović, Marija
Kremenović, Aleksandar S.
Matović, Branko
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Sphene (CaTiSiO5), a calcium titanosilicate ceramic has been prepared from a powder mixture of CaCO3, TiO2 and SiO2 using vibro-milling for homogenization and activation of precursors. During the high-pressure and high-temperature synthesis (HPS) process at 4 GPa and 1,200 A degrees C, sphene undergoes into phase transition, from room-temperature phase P2(1) /a to high-temperature phase A2/a. Evidence of that structural phase transition is given in this paper using infrared, Raman spectroscopy and X-ray powder diffraction. Rietveld refinement was employed to get the structural information of the synthesized powder. The most important structural change due to phase transition, the disappearance of the characteristic out-of-center distortion of the Ti atom and moving to the center of octahedra, was confirmed. HPS is an effective method for producing full-dense ceramics without any additives. Reduction of particle size occurred during high-pressure compaction. Microstructure and particle ...size of both phases were analyzed by scanning electron microscopy.
Кључне речи:
Sphene / Phase transition / Raman spectroscopy / X-ray diffraction / SEM / IRИзвор:
Physics and Chemistry of Minerals, 2014, 41, 10, 775-782Издавач:
- Springer Verlag
Финансирање / пројекти:
- Синтеза, процесирање и карактеризација наноструктурних материјала за примену у области енергије, механичког инжењерства, заштите животне стредине и биомедицине (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Магматизам и геодинамика Балканског полуострва од мезозоика до данас: значај за образовање металичних и неметаличних рудних лежишта (RS-MESTD-Basic Research (BR or ON)-176016)
DOI: 10.1007/s00269-014-0693-x
ISSN: 0342-1791; 1432-2021
WoS: 000344643500005
Scopus: 2-s2.0-84920260610
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Pantić, Jelena R. AU - Urbanovich, Vladimir AU - Poharc-Logar, Vesna AU - Jokić, Bojan M. AU - Stojmenović, Marija AU - Kremenović, Aleksandar S. AU - Matović, Branko PY - 2014 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5789 AB - Sphene (CaTiSiO5), a calcium titanosilicate ceramic has been prepared from a powder mixture of CaCO3, TiO2 and SiO2 using vibro-milling for homogenization and activation of precursors. During the high-pressure and high-temperature synthesis (HPS) process at 4 GPa and 1,200 A degrees C, sphene undergoes into phase transition, from room-temperature phase P2(1) /a to high-temperature phase A2/a. Evidence of that structural phase transition is given in this paper using infrared, Raman spectroscopy and X-ray powder diffraction. Rietveld refinement was employed to get the structural information of the synthesized powder. The most important structural change due to phase transition, the disappearance of the characteristic out-of-center distortion of the Ti atom and moving to the center of octahedra, was confirmed. HPS is an effective method for producing full-dense ceramics without any additives. Reduction of particle size occurred during high-pressure compaction. Microstructure and particle size of both phases were analyzed by scanning electron microscopy. PB - Springer Verlag T2 - Physics and Chemistry of Minerals T1 - Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5) EP - 782 IS - 10 SP - 775 VL - 41 DO - 10.1007/s00269-014-0693-x ER -
@article{ author = "Pantić, Jelena R. and Urbanovich, Vladimir and Poharc-Logar, Vesna and Jokić, Bojan M. and Stojmenović, Marija and Kremenović, Aleksandar S. and Matović, Branko", year = "2014", abstract = "Sphene (CaTiSiO5), a calcium titanosilicate ceramic has been prepared from a powder mixture of CaCO3, TiO2 and SiO2 using vibro-milling for homogenization and activation of precursors. During the high-pressure and high-temperature synthesis (HPS) process at 4 GPa and 1,200 A degrees C, sphene undergoes into phase transition, from room-temperature phase P2(1) /a to high-temperature phase A2/a. Evidence of that structural phase transition is given in this paper using infrared, Raman spectroscopy and X-ray powder diffraction. Rietveld refinement was employed to get the structural information of the synthesized powder. The most important structural change due to phase transition, the disappearance of the characteristic out-of-center distortion of the Ti atom and moving to the center of octahedra, was confirmed. HPS is an effective method for producing full-dense ceramics without any additives. Reduction of particle size occurred during high-pressure compaction. Microstructure and particle size of both phases were analyzed by scanning electron microscopy.", publisher = "Springer Verlag", journal = "Physics and Chemistry of Minerals", title = "Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5)", pages = "782-775", number = "10", volume = "41", doi = "10.1007/s00269-014-0693-x" }
Pantić, J. R., Urbanovich, V., Poharc-Logar, V., Jokić, B. M., Stojmenović, M., Kremenović, A. S.,& Matović, B.. (2014). Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5). in Physics and Chemistry of Minerals Springer Verlag., 41(10), 775-782. https://doi.org/10.1007/s00269-014-0693-x
Pantić JR, Urbanovich V, Poharc-Logar V, Jokić BM, Stojmenović M, Kremenović AS, Matović B. Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5). in Physics and Chemistry of Minerals. 2014;41(10):775-782. doi:10.1007/s00269-014-0693-x .
Pantić, Jelena R., Urbanovich, Vladimir, Poharc-Logar, Vesna, Jokić, Bojan M., Stojmenović, Marija, Kremenović, Aleksandar S., Matović, Branko, "Synthesis and characterization of high-pressure and high-temperature sphene (CaTiSiO5)" in Physics and Chemistry of Minerals, 41, no. 10 (2014):775-782, https://doi.org/10.1007/s00269-014-0693-x . .