Cavitation damages morphology of high-strength low-alloy steel
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Development of contemporary procedures for lead obtaining / Razvoj savremenih postupaka dobijanja olova
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Contemporary procedures of lead concentrates treatment were in different expansion during last thirty years. All procedures have in common the following: smelting reaction proceeds in solid-gas suspension, melting products ...
Dynamic recrystallization in M2 tool steel during friction welding
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Friction welding of M2 tool steel and 1730 quenched and tempered steel was performed with the aim to reveal the origin of extremely fine martensitic grain in M2 steel after welding. Taking into account thermomechanical ...
Microstructure evolution of the hot-rolled modified AA 5083 alloys during the two stage thermal treatment
(Savez inženjera metalurgije Srbije, Beograd, 2011)
The effects of the two stage heat treatment on the structure of two hot-rolled 5083 aluminum alloys without and with 0.12% Zr addition were investigated. Combination of the metallographic and transmission electron microscopy ...
A two-stage metal valorisation process from electric arc furnace dust (eafd)
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper demonstrates possibility of separate zinc and lead recovery from coal composite pellets, composed of EAFD with other synergetic iron-bearing wastes and by-products (mill scale, pyrite-cinder, magnetite concentrate), ...
The influence of thermomechanical treatment on recrystallization of AlMg4.5Cu0.5 alloy
(Savez inženjera metalurgije Srbije, Beograd, 2007)
Recrystallization behavior of an Al-Mg-Cu alloy (4.5 wt. %Mg and 0.45 wt %Cu) subjected to different thermomechanical treatments (TMTs) have been studied by means of light optical microscopy and hardness measurements. In ...