Kinetics of the hydrogen evolution reaction on Ni-(Ebonex-supported Ru) composite coatings in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The hydrogen evolution reaction (HER) was studied on Ni, Ni-Ebonex and Ni-(Ebonex-Ru) coatings in 1 mol dm(-3) NaOH solution at 25 degrees C. The composite coatings were electro-deposited from a nickel Watts-type bath ...
Hydrogen evolution in acid solution at Pd electrodeposited onto Ti2AlC
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
The hydrogen evolution reaction (HER) was studied in 0.5 M H2SO4 at 25 degrees C on Pd electrodeposited onto Ti2AlC substrate, as an excellent substrate due to its high conductivity and high stability in concentrated ...
Ru layers electrodeposited onto highly stable Ti2AlC substrates as cathodes for hydrogen evolution in sulfuric acid solutions
(Elsevier, 2016)
In this work, the hydrogen evolution reaction (HER) was studied on Ru coated Ti2AlC electrodes in 1.0 mol dm(-3) H2SO4 at 25 degrees C. Ti2AlC was found to be a highly stable substrate in sulfuric acid solutions due to the ...
Non-noble metal composite cathodes for hydrogen evolution. Part II: The Ni-MoO2 coatings electrodeposited from nickel chloride-ammonium chloride bath containing MoO2 powder particles
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
In this work the procedure of the deposition of composite Ni-MoO2 coatings onto Ni mesh from the nickel chloride-ammonium chloride electrolyte containing suspended MoO2 powder particles, under simulated industrial deposition ...
Ru layers electrodeposited onto highly stable Ti2AlC substrates as cathodes for hydrogen evolution in sulfuric acid solutions
(Elsevier, 2016)
In this work, the hydrogen evolution reaction (HER) was studied on Ru coated Ti2AlC electrodes in 1.0 mol dm(-3) H2SO4 at 25 degrees C. Ti2AlC was found to be a highly stable substrate in sulfuric acid solutions due to the ...