Formability of a high-strength Al Mg6.8 type alloy sheet
(Springer, New York, 1998)
Room temperature formability testing was performed on an AlMg6.8 type alloy sheet with a fully recrystallized structure (average grain diameter similar to 18 mu m) and after partial annealing with a retained deformed ...
Corrosion protection of aluminium by a cataphoretic epoxy coating
(Elsevier Science Sa, Lausanne, 1999)
The corrosion behavior and thermal stability of epoxy coating electrodeposited on aluminium have been investigated during exposure to 3% NaCl. Electrochemical impedance spectroscopy (EIS), gravimetric liquid sorption ...
The flow of the viscous fluid around the sphere in the range Re {similar or less-than} 2
(Springer Wien, Wien, 1992)
An improved and more correct solution of Oseen's equations, when the flow of the incompressible viscous fluid around the sphere is concerned, has been suggested. The new Oseen's correction term of the Stokes solution for ...
Shrinkage properties of wool treated with low temperature plasma and chitosan biopolymer
(Textile Research Inst, Princeton, 1999)
Low temperature plasma treatments of wool modify only the cuticle surface of the fibers, improving their surface wettability, dyeability, fiber cohesion, and shrink resistance. The shrink-resist properties obtained with ...
The thermal degradation of some isomers of poly(di-butyl itaconates)
(Elsevier, Amsterdam, 1999)
The non-oxidative and oxidative thermal degradation of poly(di-iso-butyl itaconate) (PDiBI), poly(di-n-butyl itaconate) (PDnBI), and poly(di-sec-butyl itaconate) (PDsBI) were studied by following changes in the polymer ...
Oxygen reduction reaction on Pt(111): effects of bromide
(Elsevier Science Sa, Lausanne, 1999)
Using the rotating ring-disk technique (RRDE) the oxygen reduction reaction (orr) was studied on the Pt(111) surface in the presence of Br- anions. We found that the orr at the Pt(111) \ Br-ad interface is always accompanied ...
The potential of piezoelectric sensors for characterization of activated carbon cloth applied in adsorption of phenols from air
(Amer Chemical Soc, Washington, 1998)
Characterisation of activated carbon cloth (ACC) applied for phenols adsorption from the air was performed by a pair of coated piezoelectric quartz crystals as sensors. ACC cloth was impregnated with specific organic ...
Hydrogen evolution at Zn-Ni alloys
(Pergamon-Elsevier Science Ltd, Oxford, 1998)
Zn-Ni alloys were electrodeposited from a berate-citrate and TEPA bath in potentiostatic and galvanostatic regimes. Potential of electrodeposition or current density were varied and chemical composition and phase structure ...
The use of chitosan on hydrogen peroxide pretreated wool
(Amer Assoc Textile Chemists Colorists-Aatcc, Res Triangle Pk, 1998)
Since chlorination is known to produce substantial pollution with adsorbable organo halogens (AOX) in textile wastewater, shrink resist treatments like the widely used chlorine/Hercosett process are no longer environmentally ...
Electrooxidation of H-2, CO and H-2/CO mixtures on a well-characterized Pt-Re bulk alloy electrode and comparison with other Pt binary alloys
(Pergamon-Elsevier Science Ltd, Oxford, 1998)
We report new results for the electrooxidation of Hz, CO and H-2/CO mixtures on a Pt75Re25 bulk alloy using surface preparation in a UHV chamber and characterization by X-ray photoelectron spectroscopy (XPS). Sputter-cleaned ...