Investigation of dynamic young modulus during thermal stability testing of the refractory material / Određivanje dinamičkog jungovog modula elastičnosti tokom ispitivanja termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 42 % Al2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied. Photographs of the samples before cycling, and after some number of cycles were ...
Laboratory investigation of cavitation resistance of materials: Modified ultrasonically induced cavitation test method / Laboratorijsko istraživanje kavitacione otpornosti materijala - modificirana ultrazvučna metoda
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Cavitation erosion represents an actual problem in machines, whose components such as propellers, blades of hydraulic pumps and turbines, are exposed to high-speed flow of liquid. Research exhibited that hydraulic machinery ...
Structure and kinetics of internal oxidation in Ag-Sn alloys / Struktura i kinetika interne oksidacije Ag-Sn legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Internal oxidation in Ag-Sn-In-Te and Ag-Sn-Cu-Bi alloys was tested. micro structures of casted and homogenized samples, as well as after internal oxidation were followed by optical microscopy. The structure of Ag-Sn-Cu-Bi ...
Monitoring the damage level during thermal stability testing of refractory sample using soninic measurement
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 28 % AI2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied as experimental method for thermal stability testing. Dynamic Young modulus of ...
The effects of thermomechanical treatment on the SCC resistance of highly alloyed Al-Mg sheet / Uticaj termomehaničke obrade na otpornost prema naponskoj koroziji visoko legiranih Al-Mg limova
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The effects of cold work and different heat treatments on the stress corrosion cracking (SCC) behavior of Al-Mg6.8% alloy were studied using slow strain rate testing (SSRT). The results have indicated high SCC susceptibility ...
Studies of a wear resistant cast iron / Izučavanje belih gvožđa otpornih na habanje
(Savez inženjera metalurgije Srbije, Beograd, 2003)
The objective of this investigation was to set down (on the base of the results obtained by the examination of white cast iron alloys with different content of the alloying elements) a correlation between chemical composition ...
Thermodynamic and structural investigation of the Ag-In-Sb system
(Croatian Metallurgical Society, 2007)
The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented ...
Experimental design approach regarding kinetics of high pressure leaching processes / Dizajniranje eksperimenata u pogledu na kinetiku luženja pri visokim pritiscima
(Savez inženjera metalurgije Srbije, Beograd, 2003)
Kinetics of high pressure leaching of nickel latente ore "Rudjinci", Serbia was studied in this work. The following parameters: temperature, acid to ore ratio, stirring speed, and time were optimized in order to obtain the ...
Shot-peening induced twinning in ship-building steel / Dvojnikovanje u brodskom limu kao posledica tretiranja u mlazu sačme
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The aim of this work to simulate a shot-peening process and reveal the final microstructure. The latter consisted of rafinated ferritic grains, with occurrence of twins in some grains. Since the twinning occurs when a very ...
An improved method for thermal stability behavior characterization of silicon carbide/cordierite composite material
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 50:50. Samples were exposed to the water quench test from 950°C, ...