Oxygen reduction on iron-Part VI. Processes in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1994)
The kinetics of oxygen reduction were studied on passivated iron in borate buffered and unbuffered solutions of pH ranging from 7.4 to 13.8. A rotating disk electrode was employed. The O2 reduction on iron under these ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
HCOOH oxidation on thin Pd layers on Au: Self-poisoning by the subsequent reaction of the reaction product
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The oxidation of HCOOH has been investigated on thin Pd layers ranging from 1 to 17 ML equivalents electrodeposited on polycrystalline Au substrate (Pd"Au). The results are compared to those on Pd black. Potentiodynamic ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Oxygen reduction on iron-IV. The reduction of hydrogen peroxide as the intermediate in oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1991)
The kinetics of hydrogen peroxide reduction were studied on iron in borate buffered and unbuffered solutions of pH ranging from 8.6 to 13.8, with and without the presence of chloride ions. A rotating disk electrode was ...
Hydrogen peroxide oxidation on passive iron in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1992)
The kinetics of hydrogen peroxide oxidation were studied on passive iron in alkaline solutions of pH ranging from 9.8 to 13.8, using the rotating disk electrode. Measurements were taken using the linear sweep technique. ...