Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
The influence of the cellular structure of the seed on the structure single crystal superalloy based on Ni / Uticaj ćelijske strukture klice na strukturu monokristala superlegure na bazi Ni
(Savez inženjera metalurgije Srbije, Beograd, 2003)
This paper elaborates the investigations about influence of the cellular structure of the seed to the distance between primary dendrites, λ1. Investigations were performed on superalloy single crystals based Ni which were ...
The influence of the solidification rate on the interface shape and distribution of solute
(Savez inženjera metalurgije Srbije, Beograd, 2002)
In this paper investigation of the influence of the solidification conditions on the interface shape and distribution of solute during the solidification of AI-Cu alloy by vertical Bridgman method were investigated. The ...
The influence of thermomechanical treatment and chemical composition on recrystallization of Al-Mg alloys
(Savez inženjera metalurgije Srbije, Beograd, 2007)
Recrystallization behaviour of AlMg3, AlMg4.5Mn and AlMg6Mn alloy plates subjected to different thermomechanical treatments (TMTs), has been studied by means of optical microscopy and hardness measurements. Applied two-stage ...
Hydrometallurgical process for extraction of metals from electronic waste, Part I: Material characterization and process option selection
(Savez inženjera metalurgije Srbije, Beograd, 2009)
Used electronic equipment became one of the fastest growing waste streams in the world. In the past two decades recycling of printed circuit boards (PCBs) has been based on pyrometallurgy, highly polluting recycling ...
Overview of the materials: Metals selection process / Strategija izbora metalnih materijala
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Overview of the metal material selection process will be subject of this paper. Interrelationship among design, materials and processing will be presented. Materials selection for a new design as well as materials substitution ...